The invention discloses a purification method of boron powder surface, including: with a purity of 88 ~ 95% boron powder as raw materials by ball milling treatment, boron powder particles are evenly dispersed; the uniform dispersion of particles of boron powder into high temperature in the container, then the resistance in high temperature heat treatment equipment in the container and, in a vacuum or inert gas protection conditions, heating to 1700 to 2150 DEG C, holding for 60 ~ 90min, and then cooled to room temperature, so as to achieve the purification of boron powder surface. The invention not only has simple process, easy control, and boron powder surface is not easy to form the two oxidation, the purity of boron powder surface after purification can increase from 1 to 6%, to meet the performance requirements of high energy fuel applications.
【技术实现步骤摘要】
一种硼粉表面净化方法
本专利技术涉及硼的精细化工
，尤其涉及一种硼粉表面净化方法。
技术介绍
硼粉是一种重要的硼精细化工产品，应用广泛。硼具有高热值特点，应用于燃料中能满足火箭发动机所需的高能贫氧要求。目前，工业化生产的硼粉表面含有氧化硼、多元硼化物等杂质，在高能燃料中应用时，不仅降低其自身热量，而且硼粉表面杂质成分容易与燃料药浆组分发生反应，固化后产生大量气孔、裂纹等，直接影响了高能燃料的制药工艺性能，因此要实现硼粉真正实用化，必须对硼粉表面进行净化处理。在现有技术中，用乙醇、蒸馏水等对硼粉进行提纯处理，可有效去除硼粉表面的H3BO3杂质，改善硼粉表面性能，有利于硼粉的燃烧。但这种方法采用较为复杂的湿法工艺，硼粉在处理过程中表面容易形成二次氧化。
技术实现思路
针对现有技术中的上述不足之处，本专利技术提供了一种硼粉表面净化方法，不仅加工工艺简单、操作易于控制，而且硼粉表面不易形成二次氧化，经表面净化后的硼粉纯度可提升1～6％，满足了高能燃料应用的性能需求。本专利技术的目的是通过以下技术方案实现的：一种硼粉表面净化方法，包含以下步骤：步骤A、以纯度为88～95％...
【技术保护点】
一种硼粉表面净化方法，其特征在于，包含以下步骤：步骤A、以纯度为88～95％的硼粉为原料进行球磨处理，得到均匀分散的硼粉颗粒；步骤B、将所述均匀分散的硼粉颗粒装入耐高温容器中，然后将所述耐高温容器置于热处理设备中，并在真空或惰性气体保护条件下，升温到1700～2150℃，保温60～90min，再冷却至室温，从而实现硼粉表面净化。
【技术特征摘要】
1.一种硼粉表面净化方法，其特征在于，包含以下步骤：步骤A、以纯度为88～95％的硼粉为原料进行球磨处理，得到均匀分散的硼粉颗粒；步骤B、将所述均匀分散的硼粉颗粒装入耐高温容器中，然后将所述耐高温容器置于热处理设备中，并在真空或惰性气体保护条件下，升温到1700～2150℃，保温60～90min，再冷却至室温，从而实现硼粉表面净化。2.根据权利要求1所述的硼粉表面净化方法，其特征在于，进行球磨处理的设备采用滚筒球磨机或高能行星球磨机。3.根据权利要求1或2所述的硼粉表面净化方...