一种石墨烯掺杂的二氧化钌基多孔电极及其制备方法技术

本发明专利技术属于一种电极材料技术领域，具体涉及一种石墨烯掺杂的RuO2基多孔电极及其制备方法。本发明专利技术将三氯化钌与石墨烯进行负载，然后再将其与非贵金属氧化物复合，制得一种复合型电极材料。本发明专利技术通过结合石墨烯的高导电性和高的比表面、贵金属氧化物RuO2的高导电性和活性以及非贵金属氧化物材料独特的外层电子结构，制备一种新型高比电容的多孔金属氧化物/石墨烯复合电极。

Graphene doped two ruthenium oxide based porous electrode and its preparation method

The invention belongs to the field of electrode material technology, in particular relates to a graphene doped RuO2 based porous electrode and a preparation method thereof. In the present invention, three ruthenium chloride and graphene are loaded and then combined with non noble metal oxide, and a composite electrode material is prepared. The present invention by combining graphene with high conductivity and high specific surface, noble metal oxide RuO2 with high conductivity and activity of non noble metal oxide materials and unique outer electronic structure, porous metal oxide / preparation of a new type of high specific capacitance of graphene composite electrode.

【技术实现步骤摘要】
一种石墨烯掺杂的二氧化钌基多孔电极及其制备方法
本专利技术属于一种电极材料
，具体涉及一种石墨烯掺杂的RuO2基多孔电极及其制备方法。
技术介绍
RuO2是活性最好的贵金属氧化物，以RuO2为活性物质添加非贵金属氧化物如TiO2、SnO2、Co3O4、Ni2O5中的一种或几种成为典型的析氯电极，当混合氧化物处于微晶状态时又具有很好的比电容特性。因此添加非贵金属氧化物提高其电化学性能并降低成本是研究重点。然而，添加非贵金属氧化物虽然可以有效提高以RuO2为基的氧化物材料的电容性能，但是导电性较差，而且在充放电过程中体积膨胀严重，造成电极粉化和崩塌。石墨烯的电荷载体是狄拉克费米子（Diracfermion），无数次实验证明，当粒子穿透石墨烯的时候，能发生隧道效应。和别的高比表面积碳材料相比，石墨烯的比表面积不会随着孔隙率的变化而改变，它的比表面积与自身的层数和堆积方式有关，大部分的石墨烯会紧密靠拢在一起，构成一种多孔的三维结构，其中大量的孔隙结构可以加快在石墨烯与电解液界面上的离子扩散速度，这就使得石墨烯具备充当理想的超级电容器材料的条件。本专利技术意在结合石墨烯的高导电性和高的比本文档来自技高网...

【技术保护点】
一种石墨烯掺杂的RuO2基多孔电极的制备方法，其特征在于：具体步骤为：（1）采用喷砂后的TA2钛板或泡沫Ni为基体，除油，刻蚀，用去离子水冲洗后，放入乙醇溶液中备用；（2）按照Ru的载量0.2‑0.6mg/cm

【技术特征摘要】
1.一种石墨烯掺杂的RuO2基多孔电极的制备方法，其特征在于：具体步骤为：（1）采用喷砂后的TA2钛板或泡沫Ni为基体，除油，刻蚀，用去离子水冲洗后，放入乙醇溶液中备用；（2）按照Ru的载量0.2-0.6mg/cm2取三氯化钌溶解于无水乙醇中超声震荡完全溶解；（3）按照0.2-0.6g/cm2称取石墨烯并加入0.5ml/cm2浓盐酸对石墨烯进行酸化处理，将酸化后的石墨烯混合到三氯化钌溶液，继续超声振荡；（4）取非贵金属氧化物的前驱体按1:4-4:1的贵金属离子与非贵金属离子摩尔比溶解于无...

【专利技术属性】
技术研发人员：邵艳群，何建，张帅，黄善锋，王艳鸿，
申请(专利权)人：福州大学，
类型：发明
国别省市：福建,35