一种碱金属基纳米流体CO2吸收液制造技术
An alkali metal nano fluid CO2 absorption solution
The present invention discloses an alkali metal nano fluid CO2 absorption solution. The absorption liquid in the aqueous solution of alkali metal carbonate based potassium carbonate or sodium carbonate as base liquid, wherein the alkali metal carbonate group accounted for 5% of the total mass absorption liquid to 70%, a kind of nano silicon oxide, iron oxide nanoparticles, nano zirconia, nano titanium oxide and nano Magnesium Oxide as additives, accounting for 0.1% ~ 1% of the total mass absorption liquid, as a dispersant hydroxyethyl cellulose, stearic acid, sodium dodecyl sulfate in twelve, accounting for 0.1% to 1% of the total mass absorption liquid. The invention of the CO2 absorption temperature of 10 DEG 50 DEG C, regeneration temperature is 60 DEG C 150 DEG C, and circulation transport is convenient, not easy to wear, corrosion of equipment, CO2 high removal efficiency, low energy consumption, energy saving and environmental protection.
【技术实现步骤摘要】
一种碱金属基纳米流体CO2吸收液
本专利技术涉及化石燃料燃烧产生的烟气中CO2的脱除和浓缩方法，具体涉及一种碱金属基纳米流体CO2吸收液，属于二氧化碳减排
技术介绍
随着社会工业化的不断发展，温室气体排放所造成的日趋严重的全球变暖问题成为国际社会普遍关注的焦点。以化石燃料为主要能源的电力生产中，CO2的排放量约占人类各种活动所引起的CO2排放总量的30％以上，是CO2的最大单点固定排放源。因此，研究和开发适用于燃煤电厂的CO2减排技术对控制和减缓CO2排放量急剧上升的趋势具有十分重要的战略意义。在众多CO2捕集技术中，醇胺溶液化学吸收法(MEA)是获得工业实践应用最广泛的一种方法。目前，大多数电厂都采用以MEA溶剂为基础的化学吸收法。但是，MEA法存在许多不足之处，如由于氧化、热降解、发生不可逆反应和蒸发等原因导致吸收剂吸收效率下降、吸收剂损耗、吸收剂降解产物造成系统腐蚀、再生能耗大及初投资和运作成本偏高等。因此，强化吸收剂与CO2的气液传质，进而缩小吸收塔的体积，降低设备材料成本及占地面积，是该技术研究的重点。近年来，纳米流体在传热传质领域取得的效果显...
【技术保护点】
一种碱金属基纳米流体CO2吸收液，其特征在于，所述的吸收液以碱金属基碳酸盐碳酸钾或碳酸钠的水溶液作为基液，纳米氧化硅、纳米氧化铁、纳米氧化锆、纳米氧化钛或纳米氧化镁作为添加剂，羟乙基纤维素、硬脂酸钠或十二烷基硫酸钠作为分散剂。
【技术特征摘要】
1.一种碱金属基纳米流体CO2吸收液，其特征在于，所述的吸收液以碱金属基碳酸盐碳酸钾或碳酸钠的水溶液作为基液，纳米氧化硅、纳米氧化铁、纳米氧化锆、纳米氧化钛或纳米氧化镁作为添加剂，羟乙基纤维素、硬脂酸钠或十二烷基硫酸钠作为分散剂。2.根据权利要求1所述的吸收液，其特征在于，所述的碱金属基碳酸盐占吸收液总质量的5％～70％。3.根据权利要求1所述的吸收液，其特征在于，所述...