层状二硫化钼/碳复合材料的制备方法技术
Preparation of layered molybdenum disulfide / Carbon Composites
The invention discloses a method for preparing layered MoS2 / carbon composite material, which comprises the following steps: adding methyl orthosilicate in hydrochloric acid solution, deionized water, ethanol, silicon sol; the ammonium molybdate is dissolved in deionized water, adding glucose, the added silica sol solution after static; the wet gel drying, dry tube furnace under the protection of inert gas in the gel with sulfur powder at 600 to 1000 DEG C for 3 ~ 6h, black powder; the black powder is dissolved in the aqueous solution of NaOH, from 80 to 100 DEG C standing for 18 ~ 24h, followed by centrifugation, are layered MoS2 / carbon composite material.
【技术实现步骤摘要】
层状二硫化钼/碳复合材料的制备方法
本专利技术涉及一种层状二硫化钼/碳复合材料的制备方法，特别涉及一种用于锂电池负极材料的层状二硫化钼/碳复合材料的制备方法。
技术介绍
21世纪是新能源和新材料快速发展的时代，新能源的探索可以解决人类社会日益严重的自然能源枯竭问题，性能优异的新材料的研究和应用可能会突破现在工业生产中存的一些技术瓶颈，大大提高人类社会生产力水平。因此，各个国家势必将在新能源和新材料方面展开激烈竞争。锂离子电池的出现大大改变了人类的生活。锂离子电池作为一类二次电池广泛的应用在电子产品，如：笔记本电脑、智能手机、平板电脑，以及最近新兴的可穿戴设备中。近几年，新能源汽车逐渐步入了人们的生活，而锂离子电池正是为之提供能源动力的关键。二硫化钼属于六方晶系层状结构，单层二硫化钼由三层原子层构成，其中上下两层为硫原子层被中间钼原子层隔开，形成所谓的“三明治结构”。在单层二硫化钼内，每个钼原子与六个硫原子通过共价键结合，同时每个硫原子与三个钼原子通过共价键结合。多层或块体的二硫化钼则是由这些单层“三明治结构”通过微弱的范德瓦尔斯力结合而成。由于层与层之间弱的结合力...
【技术保护点】
层状二硫化钼/碳复合材料的制备方法，其特征在于包括以下步骤：1)、将1～3mL浓度为0.01～0.5mol/L盐酸溶液加入到由1～3mL去离子水与5～10mL无水乙醇组成的混合溶液中，搅拌30～60min，得到均质溶液；2)、向步骤1)得到的均质溶液中加入1.5～3.5mL的正硅酸甲酯，在40～80℃下搅拌3～6h，得到硅溶胶；3)、将钼酸铵溶解在20～50mL的去离子水中，再加入0.5～1.5g的葡萄糖搅拌至葡萄糖溶解；所述钼酸铵与葡萄糖的摩尔比为1：0.8～2.1；4)、将步骤2)得到的硅溶胶加入到步骤3)得到的溶液中，静置3～15min后，得到湿凝胶；5)、将步骤4)...
【技术特征摘要】
1.层状二硫化钼/碳复合材料的制备方法，其特征在于包括以下步骤：1)、将1～3mL浓度为0.01～0.5mol/L盐酸溶液加入到由1～3mL去离子水与5～10mL无水乙醇组成的混合溶液中，搅拌30～60min，得到均质溶液；2)、向步骤1)得到的均质溶液中加入1.5～3.5mL的正硅酸甲酯，在40～80℃下搅拌3～6h，得到硅溶胶；3)、将钼酸铵溶解在20～50mL的去离子水中，再加入0.5～1.5g的葡萄糖搅拌至葡萄糖溶解；所述钼酸铵与葡萄糖的摩尔比为1：0.8～2.1；4)、将步骤2)得到的硅溶胶加入到步骤3)得到的溶液中，静置3～15min后，得到湿凝胶；5)、将步骤4)得到的湿凝胶于40～80℃干燥3～6天，得到干凝胶；6)、将步骤5...
【专利技术属性】
技术研发人员：郭兴忠，尹朋岸，王子晨，杨辉，
申请(专利权)人：浙江大学，
类型：发明
国别省市：浙江,33