一种预注浆施工后取芯试样的水泥含量检测方法技术
Cement content detection method for coring sample after pre grouting construction
The invention discloses a cement content after pre grouting construction of core sample detection method, the method comprises the following steps: step first, draw the standard curve of cement content detection; the second step, the determination of core samples of cement content; among them, the standard curve for the cement content and the amount of ammonium chloride consumption curve. (1) the method of the invention can detect the content of cement grouting construction after the formation of any position, any position to accurately determine the grouting effect, provide the basis for grouting, to control ground settlement purposes; (2) the method of the invention has the advantages of simple operation, high accuracy, low cost, small amount of sample.
【技术实现步骤摘要】
一种预注浆施工后取芯试样的水泥含量检测方法
本专利技术属于施工后检测领域，涉及一种注浆效果检测方法，具体为一种预注浆施工后取芯试样的水泥含量检测方法。
技术介绍
软弱土层地铁施工中采用人工冻结法加固联络通道时，可增加地层强度和稳定性，有效隔绝地下水与地下工程联系。但冻结法施工后，周围地层会产生冻胀、融沉现象，使得土体工程性质和相邻建筑物受到不良影响。一般采用预注浆的方式控制地层沉降，注浆部位选定大多依靠工程经验，工程可控性较差。注浆不到位往往导致后期地铁运营期间上下行线产生不均匀沉降，造成严重安全隐患，因此需通过检测注浆效果指导施工。目前注浆效果的检验多采用物理方法，比如雷达探测、钻孔成像、原位动力触探、电阻率等方式反映浆液扩散范围及效果，对实验仪器和操作要求高。
技术实现思路
解决的技术问题：为了克服现有技术的缺陷，获得一种适用于判断任一位置的注浆效果，且操作简便、精确度高、成本低、取样量小的检测方法，本专利技术提供了一种预注浆施工后取芯试样的水泥含量检测方法。技术方案：一种预注浆施工后取芯试样的水泥含量检测方法，所述方法包括以下步骤：第1步、绘制水泥含量检测标准曲...
【技术保护点】
一种预注浆施工后取芯试样的水泥含量检测方法，其特征在于，所述方法包括以下步骤：第1步、绘制水泥含量检测标准曲线；第2步、测定取芯试样水泥含量；其中，所述标准曲线为水泥含量与氯化铵消耗量的关系曲线。
【技术特征摘要】
1.一种预注浆施工后取芯试样的水泥含量检测方法，其特征在于，所述方法包括以下步骤：第1步、绘制水泥含量检测标准曲线；第2步、测定取芯试样水泥含量；其中，所述标准曲线为水泥含量与氯化铵消耗量的关系曲线。2.根据权利要求1所述的一种预注浆施工后取芯试样的水泥含量检测方法，其特征在于，所述绘制水泥含量检测标准曲线的具体步骤如下：(1)用现场取出的原状土与配制好的水泥浆制作7个浓度梯度的水泥土试样；(2)将水泥土试样置于烘箱中，烘干后取出，研磨成粉；(3)取步骤(2)研磨获得的水泥土粉末，加纯水搅拌，静置，取上层悬浊液，离心；(4)取步骤(3)离心后的上清液，加入酚酞试剂，用氯化铵溶液滴定至无色，记录消耗量，7个试样滴定完成后，绘制水泥含量与氯化铵消耗量的...
【专利技术属性】
技术研发人员：杨平，潘荣凯，何文龙，万朝栋，张婷，
申请(专利权)人：南京林业大学，中铁十八局集团有限公司，
类型：发明
国别省市：江苏,32