The invention discloses a method, preparation of a flame retardant fabric including padding, two padding, drying, baking, washing, drying processes six, first into the working fluid in flame retardant fabric padding, a padding after half an hour into the flame retardant stable liquid for two times of padding, half small when removed after drying, the drying temperature is 90 DEG C, drying after high temperature baking stereotypes, baking temperature of 180 degrees, 10 minutes, 20 minutes after washing, washing drying to obtain the product again. The method has the advantages of low cost and simple preparation process, and can effectively improve the flame retardant property of the fabric and improve the safety performance.
【技术实现步骤摘要】
一种阻燃性面料的制备方法
本专利技术涉及阻燃面料领域，特别是涉及一种阻燃性面料的制备方法。
技术介绍
当前行业中，阻燃面料的制备工艺相对复杂，且所用材料价格高昂，，产品性价比较低，如何生产一种制备工艺简单，成本低廉同时阻燃性能好的产品，是一个值得研究开发的方向。
技术实现思路
本专利技术主要解决的技术问题是提供一种阻燃性面料的制备方法，成本低廉、制备工艺简单，能够有效提高面料的阻燃性能，提高安全性能。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种阻燃性面料的制备方法，包括：浸轧、二次浸轧、烘干、烘焙、水洗、烘干六道工序，首先将面料放入阻燃工作液中浸轧，浸轧半小时后放入阻燃稳定液中进行二次浸轧，半小时后取出烘干，烘干温度为90℃，烘干后进行高温烘焙定型，烘焙温度为180℃，10分钟后取出，进行水洗，水洗20分钟后再次烘干，获得成品。在本专利技术一个较佳实施例中，所述阻燃工作液成分为阻燃剂，缓冲剂，催化剂，配比为2:1:1。在本专利技术一个较佳实施例中，所述阻燃稳定液成分为稳定剂，柔软剂、固着剂，配比为1:2:1。本专利技术的有益效果是：本专利技术成本低廉、制备工艺简单，能够有效提高面料的阻燃性能，提高安全性能。具体实施方式下面对本专利技术的较佳实施例进行详细阐述，以使本专利技术的优点和特征能更易于被本领域技术人员理解，从而对本专利技术的保护范围做出更为清楚明确的界定。本专利技术实施例包括：一种阻燃性面料的制备方法，包括：浸轧、二次浸轧、烘干、烘焙、水洗、烘干六道工序，首先将面料放入阻燃工作液中浸轧，浸轧半小时后放入阻燃稳定液中进行二次浸轧，半小时后...
【技术保护点】
一种阻燃性面料的制备方法，其特征在于，包括：浸轧、二次浸轧、烘干、烘焙、水洗、烘干六道工序，首先将面料放入阻燃工作液中浸轧，浸轧半小时后放入阻燃稳定液中进行二次浸轧，半小时后取出烘干，烘干温度为90℃，烘干后进行高温烘焙定型，烘焙温度为180℃，10分钟后取出，进行水洗，水洗20分钟后再次烘干，获得成品。
【技术特征摘要】
1.一种阻燃性面料的制备方法，其特征在于，包括：浸轧、二次浸轧、烘干、烘焙、水洗、烘干六道工序，首先将面料放入阻燃工作液中浸轧，浸轧半小时后放入阻燃稳定液中进行二次浸轧，半小时后取出烘干，烘干温度为90℃，烘干后进行高温烘焙定型，烘焙温度为180℃，10分钟后取出，进行水洗...