手机壳体及其表面处理方法技术
Mobile phone shell and surface treatment method thereof
Including a mobile phone shell surface treatment method, the mobile phone shell: electro polishing processed electrolytic degreasing; the activation of acid electrolytic polishing processing on the mobile phone of the mobile phone shell; the shell of nickel plating; and the mobile phone shell drying. The polishing process was replaced by the activated acid with good light effect, and the polishing process was used to replace the general activation process. The brightness of the product was dimmed by polishing, and then the nickel was directly plated with nickel. The brightness of the coating became dark. In addition, a mobile phone shell obtained by adopting the above method is also provided.
【技术实现步骤摘要】
手机壳体及其表面处理方法
本专利技术涉及手机配件
，具体涉及手机壳体及其表面处理方法。
技术介绍
手机的配色的表面处理一般有两种：手机塑料外壳表面处理和手机金属外壳表面处理。从素色到五颜六色，主要是因为原材料的多样化、涂料、镀色技术以及表面处理工艺提升了。手机金属外壳的主要原料有：不锈钢、镁铝合金、阳极氧化铝和微弧氧化铝。主要表面处理方式有：喷砂(形成哑光珍珠银面)、抛光(形成镜面)、拉丝(形成类似缎面效果)、刻蚀(刻出各种纹理图案)、电镀(覆盖一层其他金属)、PVD、喷涂(覆盖其他非金属涂层)、镭雕、高光切削、阳极氧化和微弧氧化。目前有一种铁青铜手机壳体电镀需要镀镍，并且要求镀层亮度不能太亮，以免影响后工段检测。一般地，铁青铜手机壳体电镀前经过蚀刻，电抛，依照正常的前处理工艺处理后电镀镍时，镀层比较光亮，无法达到工段检测需求。如何将铁青铜手机壳体镀镍的镀层亮度调暗，是需要解决的技术问题。
技术实现思路
基于此，有必要提供一种能将铁青铜手机壳体镀镍的镀层亮度调暗的手机壳体表面处理方法。一种手机壳体表面处理方法，包括下述步骤：将电抛光处理后的手机壳体进行电解除油；...
【技术保护点】
一种手机壳体表面处理方法，其特征在于，包括下述步骤：将电抛光处理后的手机壳体进行电解除油；将电解除油后的手机壳体于活化酸中进行电解抛光处理，所述活化酸由浓硫酸与双氧水组成；对抛光后的手机壳体进行镀镍处理；及将镀镍处理后的手机壳体烘干处理。
【技术特征摘要】
1.一种手机壳体表面处理方法，其特征在于，包括下述步骤：将电抛光处理后的手机壳体进行电解除油；将电解除油后的手机壳体于活化酸中进行电解抛光处理，所述活化酸由浓硫酸与双氧水组成；对抛光后的手机壳体进行镀镍处理；及将镀镍处理后的手机壳体烘干处理。2.根据权利要求1所述的手机壳体表面处理方法，其特征在于，在将电抛光处理后的手机壳体进行电解除油的步骤中，具体为：在温度50-70℃的碱性溶液中，以所述手机壳体为阴极，在直流电作用下将所述手机壳体表面的油污除去。3.根据权利要求2所述的手机壳体表面处理方法，其特征在于，所述碱性溶液包括氢氧化钠溶液或硅酸钠溶液或碳酸钠溶液中的至少一种，所述碱性溶液的浓度在30g/L-80g/L之间。4.根据权利要求1所述的手机壳体表面处理方法，其特征在于，所述活化酸中所述浓硫酸与所述双氧水体积比为4％-8％：6％-10％。5.根据权利要...
【专利技术属性】
技术研发人员：黄秀平，
申请(专利权)人：深圳市长盈精密技术股份有限公司，
类型：发明
国别省市：广东,44