The invention discloses a preparation method of cobalt based composite ceramic powder for dental 3D printing, the powder and ceramic powder of cobalt chromium alloy for 100: 0.5 ~ 10 mass ratio, on the ball after ball milling, and then through the carrier gas injected into argon plasma torch, by the power of 55 ~ 65KW, frequency 3 ~ ar RF plasma generator of 4MHz RF plasma ball, with cobalt based ceramic composite powder of spherical. In the invention relates to a method for preparing cobalt based composite ceramic powder in laser melting process, ceramic and metal substrate with high strength, good wettability, 3D printing molding preparation not only low thermal expansion coefficient, and good tensile properties.
【技术实现步骤摘要】
一种齿科3D打印用钴基复合陶瓷粉末的制备方法
本专利技术涉及一种金属基陶瓷复合材料，特别是涉及一种3D打印用金属基陶瓷复合粉末的制备方法。
技术介绍
用于制造义齿内冠的合金材料主要有钛合金、钴铬合金和不锈钢。近年来，3D打印技术被越来越广泛地应用于人体植入物的个性化定制，特别是义齿金属内冠的制造。通过3D打印技术制造的义齿金属内冠在力学性能上与传统铸造方法制造的金属内冠相差无几，甚至在致密度、拉伸强度等某些性能方面还要优于铸造金属内冠。再加上3D打印技术具有速度快、节省材料、节省人工成本等优势，在义齿金属內冠的制造方面应用前景非常广阔。义齿金属内冠制作完成后，还需要在其表面进行烤瓷。即在金属内冠表面涂上与天然牙相似的瓷粉，在烤瓷炉内真空高温烧结，使瓷粉与金属内冠结合在一起，冷却后制成烤瓷牙。如果烤瓷层与金属内冠基底间的热膨胀系数差异过大，冷却时会产生残余应力，导致烤瓷层剥落或开裂。为了使烤瓷层与金属间具有良好的结合性，两者的热膨胀系数差值为0.5～1.0×10-6/℃时最为理想。然而，用于制作瓷粉的陶瓷材料的热膨胀系数大部分小于10×10-6/℃，而使用金属制作的...
【技术保护点】
一种齿科3D打印用钴基复合陶瓷粉末的制备方法，是将医用钴铬合金粉末与陶瓷粉末按照100∶0.5～10的质量比混合，于球磨机中球磨得到钴基陶瓷复合粉末原料；再将所述钴基陶瓷复合粉末原料以载气喷入氩等离子体炬中进行射频等离子球化，以获得球形化的钴基陶瓷复合粉末；其中，所述氩等离子体炬中的等离子体是由功率55～65KW、频率3～4MHz的射频等离子体发生器产生的。
【技术特征摘要】
1.一种齿科3D打印用钴基复合陶瓷粉末的制备方法，是将医用钴铬合金粉末与陶瓷粉末按照100∶0.5～10的质量比混合，于球磨机中球磨得到钴基陶瓷复合粉末原料；再将所述钴基陶瓷复合粉末原料以载气喷入氩等离子体炬中进行射频等离子球化，以获得球形化的钴基陶瓷复合粉末；其中，所述氩等离子体炬中的等离子体是由功率55～65KW、频率3～4MHz的射频等离子体发生器产生的。2.根据权利要求1所述的制备方法，其特征是所述医用钴铬合金粉末的粒径为20～55µm。3.根据权利要求1所述的制备方法，其特征是所述的陶瓷粉末是Al2O3、SiC、ZrO2、SiO2、Si3N4中的一种，或几种的任意比例混合物。4.根据权利要求3所述的制备方法，其特征是所述陶瓷粉末的粒径为50～400n...