合金螺杆制造技术
Alloy screw
The alloy screw, including rod head, screw, connector, rod cap, rod, Ni Cr alloy coating, aluminum magnesium alloy coating and nickel base alloy teeth, the surface of the screw rod and screw, covered with two layers of Ni Cr alloy coating and aluminum magnesium alloy coated composite powder coating, composition of alloy powder the Ni Cr alloy and aluminum magnesium alloy powder composite coating, Ni Cr alloy powder includes 70 80%, 20 and 30% aluminum magnesium alloy powder, the powder particle size of 200 400 mesh, the coating is uniform, uniform thickness is covered by the screw and the screw teeth on the surface, the thickness of 0.35mm; secondly on the outer surface is covered with a layer of nickel base alloy component is serrated, nickel base alloy powder particle size is 400 mesh 300; the invention has the advantages of saving resources, reduce the cost.
【技术实现步骤摘要】
合金螺杆
本专利技术涉及合金螺杆，具体涉及一种杆体及螺牙表面上覆盖有两层镍铬合金与铝镁合金复合粉末涂层以及镍基合金锯齿的耐磨耐腐蚀耐高温高强度的合金螺杆。
技术介绍
目前我国常用的螺杆材料有45号钢、40Cr、氨化钢、38CrMOAl，高温合金等，现有技术的螺杆制造方法多采用氮化后再电镀硬铬。螺杆往往是在高温、一定腐蚀、强烈磨损、大扭矩下工作的，由于工作时螺杆磨损严重、并且不耐腐蚀，其寿命较短，一般只有几个月，并且工作过程中会影响产品的质量，往往造成产品质量不稳定，成品率较低，因而严重浪费资源，其生产成本居高不下。
技术实现思路
本专利技术的目的是提供合金螺杆，针对现有技术螺杆存在的上述不足，提供一种具有耐磨耐腐蚀耐高温高强度的复合粉末涂层以及镍基合金锯齿，具有良好的耐磨、耐腐蚀、耐高温、高强度、且不易变形、工作稳定性好、寿命较长的合金螺杆。本专利技术为实现上述目的所采用的技术方案是：合金螺杆，包括杆头、螺牙、连接体、杆帽、杆体、镍铬合金涂层、铝镁合金涂层和镍基合金锯齿，所述螺杆杆体及螺牙的表面上，覆盖有两层镍铬合金涂层与铝镁合金涂层复合粉末涂层，构成该镍铬合金与铝镁...
【技术保护点】
合金螺杆，包括杆头(1)、螺牙(2)、连接体(3)、杆帽(4)、杆体(5)、镍铬合金涂层(6)、铝镁合金涂层(7)和镍基合金锯齿(8)，其特征是：所述螺杆杆体(5)及螺牙(2)的表面上，覆盖有两层镍铬合金涂层(6)与铝镁合金涂层(7)复合粉末涂层，构成该镍铬合金与铝镁合金复合粉末涂层的合金粉末，包括70‑80%的镍铬合金粉末，及20‑30%铝镁合金粉末，该粉末粒度为200‑400目，该涂层是呈整体均匀、厚度一致地覆盖所述螺杆本体及螺牙（2）的表面上，其厚度为0.35mm；其次在外表面还覆盖有一层镍基合金锯齿（8），成分为镍基合金粉末，粉末粒度为300‑400目。
【技术特征摘要】
1.合金螺杆，包括杆头(1)、螺牙(2)、连接体(3)、杆帽(4)、杆体(5)、镍铬合金涂层(6)、铝镁合金涂层(7)和镍基合金锯齿(8)，其特征是：所述螺杆杆体(5)及螺牙(2)的表面上，覆盖有两层镍铬合金涂层(6)与铝镁合金涂层(7)复合粉末涂层，构成该镍铬合金与铝镁合金复合粉末涂层的合金粉末，包括70-80%的镍铬合金粉末，及20-3...