The invention discloses a stable and efficient black phosphating at room temperature pre infusion, the per liter of solution is composed of the following ingredients: the weight of 1 10g blackening agent, blackening agent 0.1 1g, 0.5 5g, stabilizer accelerator 1 5g, the balance of water. The pre infusion of the invention can realize high density on the surface of iron and steel, adhesion work, uniform appearance. And because the conversion film is a dense crystalline structure, the corrosion resistance of the pre infusion can significantly enhance the phosphate conversion film, and the pre infusion is extremely stable, large treatment capacity, does not contain nickel, nitrite and other toxic and harmful substances, little pollution to the environment.
【技术实现步骤摘要】
一种稳定高效的常温黑色磷化预浸液
本专利技术主要涉及表面化学领域，尤其涉及一种稳定高效的常温黑色磷化预浸液。
技术介绍
黑色磷化处理是一种被广泛采用的价廉质优的表面处理技术。在工业大气环境及海洋性气侯条件下,其耐蚀性比普通磷化膜高数倍，比氧化膜、常温发黑膜高数十倍，表现出优异的耐蚀性能和优秀的黑色外观颜色。而且这种膜层还具有吸光、吸热、绝缘等性能。另外，钢铁黑色磷化工艺具有生产成本低、产品质量好、节能污染小等先进的技术、经济指标。目前，国内外市场上一些航空、电子、兵器、船舶、汽车、机电等零部件、标准件、紧固件等大多黑色磷化膜代替了以往的磷化膜、氧化膜，拥有着广泛的应用成果。钢铁的黑膜磷化工艺大致可分为２种：一种是一步法，即不需预浸可直接磷化，现有的一步法黑色磷化多为锰盐高温磷化，但是该膜层易出现结晶粗大、磷化液沉渣较多等问题，调整起来较为复杂，工艺操作温度高，耗能大，且产品黑度差。另一种是二步法，即先预浸再磷化，预浸液能够大幅降低后续磷化工序的操作温度，大大提高磷化膜的黑度，故预发黑处理液的作用至关重要。但是，目前市场上绝大多数的预浸液极不稳定，易掉膜，这样就会造...
【技术保护点】
一种稳定高效的常温黑色磷化预浸液，其特征在于，每升所述的稳定高效的常温黑色磷化预浸液是由下述重量的各原料混合制得：发黑剂1‑10g、发黑助剂0.1‑1g、稳定剂 0.5‑5g、促进剂1‑5g、余量为水；所述的发黑剂由下述重量份的各原料组成的：30‑50份的65%的硝酸在不断搅拌条件下慢慢加入到40‑65份净化水中，得稀硝酸溶液；后将 5‑10份硝酸铋慢慢加入到上述稀硝酸溶液中，常温下反应120‑150min，反应过程中施加功率为75‑85W的超声波并施加搅拌，反应完毕后，即得发黑剂。
【技术特征摘要】
1.一种稳定高效的常温黑色磷化预浸液，其特征在于，每升所述的稳定高效的常温黑色磷化预浸液是由下述重量的各原料混合制得：发黑剂1-10g、发黑助剂0.1-1g、稳定剂0.5-5g、促进剂1-5g、余量为水；所述的发黑剂由下述重量份的各原料组成的：30-50份的65%的硝酸在不断搅拌条件下慢慢加入到40-65份净化水中，得稀硝酸溶液；后将5-10份硝酸铋慢慢加入到上述稀硝酸溶液中，常温下反应120-150min，反应过程中施加功率为75-85W的超声波并施加搅拌，反应完毕后，即得发黑剂。2.根据权利要求1所述的一种稳定高效的常温黑色磷化预浸液，其特征在于，所述的发黑助剂为硝酸铜、碳酸铜、硫酸铜中的一种或几种的混合物。3.根据权利要求1所述的一种稳定高效的常温黑色磷化预浸液，其特征在于，所述的稳定剂由下述重量份的各原料组...
【专利技术属性】
技术研发人员：王成林，
申请(专利权)人：安徽江南机械有限责任公司，
类型：发明
国别省市：安徽,34