一种两亲性气凝胶及制备方法技术
A kind of two amphiphilic aerogels and its preparation method
The invention discloses a two amphipathic aerogel and preparation method, the preparation method comprises the following steps: A, graphite oxide by ultrasonic treatment, formation of graphene oxide dispersed in the liquid; B, graphene oxide dispersed into phosphate compounds, liquid and stirring; C, stirring the mixed solution of the heating reaction, obtain functional hydrogels; D, functional hydrogels to displace the solvent, and then dried to obtain two hydrophobic aerogels. Through the method of the invention, two hydrophobic aerogels prepared with characteristics of super absorbent, has important application prospect as the catalyst carrier in the interfacial polymerization, the adsorption of heavy metal ions and emulsion breaking, oil-water separation etc..
【技术实现步骤摘要】
一种两亲性气凝胶及制备方法
本专利技术涉及石墨烯材料领域，尤其涉及一种两亲性气凝胶及制备方法。
技术介绍
石墨烯气凝胶是以石墨烯或石墨烯类材料通过一定方式，以获得石墨烯水凝胶为前提，经干燥进一步把凝胶内部水替代成空气，从而获得石墨烯气凝胶。石墨烯气凝胶自浙江大学高超课题组制备出超轻石墨烯气凝胶后，掀起一股科学研究热潮，许多科学家制备出石墨烯气凝胶或复合材料的石墨烯基气凝胶，被广泛应用于各种领域。由于石墨烯具有超疏水的特性，因此以石墨烯制备的气凝胶也具有超疏水特性。但现有的技术所制备的石墨烯气凝胶并不具有超吸水的特性，这限制了石墨烯气凝胶的应用。因此，现有技术还有待于改进和发展。
技术实现思路
鉴于上述现有技术的不足，本专利技术目的在于提供一种两亲性气凝胶及制备方法，旨在解决现有技术中石墨烯气凝胶不具备亲水性的问题。本专利技术的技术方案如下：一种两亲性气凝胶的制备方法，其中，包括步骤：A、对氧化石墨进行超声处理，形成均匀的氧化石墨烯分散液；B、在氧化石墨烯分散液中加入磷酸化合物，并搅拌；C、将搅拌后的混合液进行加热反应，获得功能化水凝胶；D、对功能化水凝胶进行溶剂置换，...
【技术保护点】
一种两亲性气凝胶的制备方法，其特征在于，包括步骤：A、对氧化石墨进行超声处理，形成均匀的氧化石墨烯分散液；B、在氧化石墨烯分散液中加入磷酸化合物，并搅拌；C、将搅拌后的混合液进行加热反应，获得功能化水凝胶；D、对功能化水凝胶进行溶剂置换，再进行干燥获得两亲性气凝胶。
【技术特征摘要】
1.一种两亲性气凝胶的制备方法，其特征在于，包括步骤：A、对氧化石墨进行超声处理，形成均匀的氧化石墨烯分散液；B、在氧化石墨烯分散液中加入磷酸化合物，并搅拌；C、将搅拌后的混合液进行加热反应，获得功能化水凝胶；D、对功能化水凝胶进行溶剂置换，再进行干燥获得两亲性气凝胶。2.根据权利要求1所述的两亲性气凝胶的制备方法，其特征在于，所述磷酸化合物为乙二胺四亚甲基磷酸、亚甲基二磷酸、氨基三亚甲基磷酸或六亚甲基二胺四亚甲基膦酸中的一种或多种。3.根据权利要求1所述的两亲性气凝胶的制备方法，其特征在于，所述步骤B中，还加入还原剂。4.根据权利要求3所述的两亲性气凝胶的制备方法，其特征在于，所述还原剂为抗坏血酸、亚硫酸氢钠或水合肼。5.根据权利要求1所述的两亲性气凝胶的制...
【专利技术属性】
技术研发人员：朱才镇，赵昱，廖伟冬，杨波，海洋，邱昭政，徐坚，
申请(专利权)人：深圳大学，
类型：发明
国别省市：广东,44