The heat treatment method of the invention Aluminum Alloy, which comprises the following steps: 1), the alloys were pre deformation at room temperature; 2), at 520 to 550 DEG C insulation 2 ~ 5h, then at 35 - 5 Deg. C water quenching of 2min; 3) 176 to 184 DEG C aging 8 ~ 16h then, air cooling. Compared with the traditional T6 heat treatment, the deformation of the heat treatment process of the invention adopts solid solution before the introduction of pre deformation, the Al Cu Mn the strength of alloy increases while plastic has been greatly enhanced and the strength increased by 7.3%, the elongation increased by 35.69%, reached 450.9MPa and 17.26% respectively.
【技术实现步骤摘要】
一种铝合金形变热处理方法
本专利技术属于铝合金热处理
，具体为一种铝合金形变热处理方法。
技术介绍
Al-Cu合金属于2xxx系铝合金，具有良好的高低温性能、较高的比强度、良好的焊接性能及断裂韧性，广泛运用于航空航天领域。Al-Cu-Mn系合金作为典型的2xxx铝合金，其工作温度为-250℃～300℃，是航空航天常用的结构材料，如大运载火箭焊接氧化剂槽以及超音速飞机蒙皮及结构零件等。通常情况下，在固溶处理之后、时效处理之前，对2xxx合金进行适当的冷变形可以起到调控组织和改善力学性能的效果。但实践中发现，合金经热处理后虽然强度得到提高，但未能很好起到提高塑性的效果。所以，针对Al-Cu-Mn系合金，需要开发一种热处理工艺，能够在提高合金强度的同时也能提高塑性。
技术实现思路
为解决现有技术存在的铝合金热处理后虽然强度得到提高，但未能很好起到提高塑性的效果的缺陷，本专利技术提供一种铝合金形变热处理方法。一种铝合金形变热处理方法，包括以下步骤：1)、室温预变形处理将合金在室温条件下进行轧制/压缩预变形，预变形量为3％～35％，且变形量一次完成；优选的预变形量为5％、...
【技术保护点】
一种铝合金形变热处理方法,其特征在于，包括以下步骤：1)、室温预变形处理将合金在室温条件下进行轧制/压缩预变形；2)、固溶处理将预变形后的合金先在520℃～550℃保温2～5h，然后在35℃±5℃水中淬火2min，其中淬火转移在10s内完成；3)时效处理将铝合金放入电热恒温鼓风干燥箱中176～184℃下时效处理8～16h，然后进行空冷。
【技术特征摘要】
1.一种铝合金形变热处理方法,其特征在于，包括以下步骤：1)、室温预变形处理将合金在室温条件下进行轧制/压缩预变形；2)、固溶处理将预变形后的合金先在520℃～550℃保温2～5h，然后在35℃±5℃水中淬火2min，其中淬火转移在10s内完成；3)时效处理将铝合金放入电热恒温鼓风干燥箱中176～184℃下时效处理8～16h，然后进行空冷。2.如权利要求1所述的铝合金形变热处理方法,其特征在于，步骤1)中的预变形量为3％～35％，且变形量一次完成。3.如权利要求2所述的铝合金形变热处理方法,其特征在于，步骤1)中的预变形量20％。4.如权利要求1所述的铝合金形变热处理方法,其特征在于，步骤2)中的合金在535℃保温3h。5.如权利要求1所述的铝合金形变热处理方法,其特征在于，步骤3)中在电热恒温鼓风干燥箱中180℃下时效处理12h。6.如权利要求1-5任一项所述的铝合金形变热处理方法,其特...
【专利技术属性】
技术研发人员：卢雅琳，周刚，王健，李兴成，周东帅，百志好，
申请(专利权)人：江苏理工学院，
类型：发明
国别省市：江苏,32