一种高硬高强人造石英石装饰板材制造方法技术
Manufacturing method of artificial marble plate with high rigidity and high strength
The invention discloses a manufacturing method of a hard hard and high strength artificial quartz decorative plate, comprising a quartz stone formula and a manufacturing process of a plate. The beneficial effect of the invention is to improve material with high hardness and high strength and high gloss flame retardant wear resistance, especially nano fumed silica, alkali resistant glass fiber added, improves the strength and hardness, added to the profile of two substances made in the final not resolved, the patent belongs to the first mentioned in the literature, blank vibration molding, rolling edge level side feeding, repeated rolling, ensure all parts of billet thickness and hardness uniform, Standard Specification for final parts, consistent.
【技术实现步骤摘要】
一种高硬高强人造石英石装饰板材制造方法
本专利技术涉及板材制造领域，特别是一种高硬高强人造石英石装饰板材制造方法。
技术介绍
现有板材市场大部分都是硬度，强度上去了，但是阻燃耐热性差，本专利技术提供了一种高硬高强人造石英石装饰板材制造方法，有效解决了这一问题。
技术实现思路
本专利技术的目的是为了解决上述问题，设计了一种高硬高强人造石英石装饰板材制造方法。实现上述目的本专利技术的技术方案为，一种高硬高强人造石英石装饰板材制造方法，石英石配方重量配比为：10-20％5目石英砂、10-20％50目石英砂、10-20％100目石英粉、10-20％300目石英粉、10-15％5目碎玻璃、3-5％30目碎玻璃、3-10％纳米气相二氧化硅、7-10％环氧树脂或复合压克力树脂、0.1％-1％硅烷偶联剂、0.8-1.2％过氧化甲乙酮、0.005-0.1％色粉、0.3-0.5％耐碱玻璃纤维。所述石英石板材制造方法：步骤一、主料预处理，对原材料去杂提纯，去除原材料中可能含有的土、沙、纸屑、木屑、金属碎等杂质，保证原材料洁净无杂质，将石英、玻璃物质混合，加入高能震动研磨机内研磨30-60分...
【技术保护点】
一种高硬高强人造石英石装饰板材制造方法，其特征在于，石英石配方重量配比为：
【技术特征摘要】
1.一种高硬高强人造石英石装饰板材制造方法，其特征在于，石英石配方重量配比为：。2.根据权利要求1所述的一种高硬高强人造石英石装饰板材制造方法，其特征在于，所述石英石板材制造方法：步骤一、主料预处理，对原材料去杂提纯，去除原材料中可能含有的土、沙、纸屑、木屑、金属碎等杂质，保证原材料洁净无杂质，将石英、玻璃物质混合，加入高能震动研磨机内研磨30-60分钟，使玻璃表面粗糙化；步骤二、将预处理好的主料及其他配方物质混合在一起，液体物质混合过程中缓慢淋入，然后均匀搅拌混合15-20分钟；步骤三、混合好的原料放入震动成型机内，根据所生产型材长、宽、厚度尺寸对布料的平整度和厚度均匀调整，分多次加入，边震动辊压边平整边加料，逐层进行，直到预设厚度；步骤四、将坯料随同模具置入平板真空震动压铸机内...
【专利技术属性】
技术研发人员：田野，
申请(专利权)人：上海正邻机电自动化设备有限公司，
类型：发明
国别省市：上海,31