The invention discloses a high-efficient welding method of E690 high strength steel tube, through the selection of welding consumables and welding process in two steps, efficient completion of welding of E690 high strength steel tube; the submerged arc welding for protecting slag, solder welding slag can prevent air intrusion of molten pool, can also reduce the cooling rate of the weld heat insulation. And ensure the mechanical properties of joints; welding parameters preset, ensure the stability of welding parameters, arc stability, easy slag removal, weld bead appearance, smooth surface, forming weld composition is uniform; the invention has low requirement to the welder, X ray inspection pass rate reached more than 99%.
【技术实现步骤摘要】
一种E690高强度钢筒体的高效焊接方法
本专利技术涉及一种焊接方法，具体涉及一种E690高强度钢筒体的高效焊接方法。
技术介绍
E690高强钢筒体是自升式风电安装船的桩腿主结构，是非常关键和核心的部件。目前国内海工产品中E690此类高强度淬火回火钢的焊接普遍采用手工焊条电弧焊或者药芯焊丝CO2气体保护焊。其对焊接的要求、焊条烘焙和领用回收要求、焊丝的防潮保存要求等很高。上述方法熔敷效率不高、焊接速度较慢、应用成本较高、飞溅大，气孔、未熔合、未焊透等缺陷产生几率大，焊条脱渣性等也较差。同时焊接弧光、噪声、烟尘、有害气体对焊工伤害大。
技术实现思路
本专利技术的目的在于针对现有技术的不足，现提供一种电弧稳定，易脱渣、焊缝表面光洁、焊道成型美观、焊缝成分也均匀的E690高强度钢筒体的高效焊接方法。为解决上述技术问题，本专利技术采用的技术方案为：一种E690高强度钢筒体的高效焊接方法，其创新点在于：经过焊材的选择和焊接工艺两个步骤，完成E690高强度钢筒体的高效焊接；具体步骤如下：（1）焊材的选择：选用的焊丝为FLUXOCORD42和OP121TTW两种焊丝，所述焊剂为氟碱性...
【技术保护点】
一种E690高强度钢筒体的高效焊接方法，其特征在于：经过焊材的选择和焊接工艺两个步骤，完成E690高强度钢筒体的高效焊接；具体步骤如下：（1）焊材的选择：选用的焊丝为FLUXOCORD42和OP121TTW两种焊丝，所述焊剂为氟碱性型烧结焊剂；（2）焊接工艺：a.采用半自动火焰切割的方法对E690高强钢筒体坡口进行切割，清理前焊缝坡口周围30‑50mm范围内的油、锈、氧化物及其它杂质，直至露出金属光泽；b.将E690高强钢筒体装配时进行内壁齐平，如若有错口，则错口值为3mm；c.对待焊区采用电预热进行预热，所述预热范围为待焊区域150mm范围；d.进行焊接工艺，焊接分为打底...
【技术特征摘要】
1.一种E690高强度钢筒体的高效焊接方法，其特征在于：经过焊材的选择和焊接工艺两个步骤，完成E690高强度钢筒体的高效焊接；具体步骤如下：（1）焊材的选择：选用的焊丝为FLUXOCORD42和OP121TTW两种焊丝，所述焊剂为氟碱性型烧结焊剂；（2）焊接工艺：a.采用半自动火焰切割的方法对E690高强钢筒体坡口进行切割，清理前焊缝坡口周围30-50mm范围内的油、锈、氧化物及其它杂质，直至露出金属光泽；b.将E690高强钢筒体装配时进行内壁齐平，如若有错口，则错口值为3mm；c.对待焊区采用电预热进行预热，所述预热范围为待焊区域150mm范围；d.进行焊接工艺，焊接分为打底焊、填充焊和盖面焊，分别形成打底焊层、填充焊层和盖面焊层，所述打底焊层的厚...
【专利技术属性】
技术研发人员：杜高峰，
申请(专利权)人：南通振华重型装备制造有限公司，
类型：发明
国别省市：江苏,32