纤维强化树脂螺栓制造技术
Fiber reinforced resin bolt
The present invention relates to a fiber reinforced resin bolt (10) and (20) formed from a resin composition containing a reinforcing fiber in a resin. The thread pitch P of the screw thread is 1.5 to 2 times of the standard pitch of the screw thread of the outer diameter of D, which is the standard of coarse metric tooth thread, uniform standard coarse tooth thread and unified standard fine tooth thread. The average fiber length of reinforced fiber is 1 to 1/3 times of pitch, and the ratio of reinforcement fiber is 20% to 80%. This provides a fiber reinforced resin bolt for strength enhancement of threaded teeth.
【技术实现步骤摘要】
【国外来华专利技术】纤维强化树脂螺栓
本专利技术涉及使用树脂中含有强化纤维的树脂组合物作为原材料的纤维强化树脂螺栓。
技术介绍
以往，在要求耐化学药品性、耐腐蚀性、生物适应性、防爆性、轻量性、保温性的领域，进行物品彼此的紧固、运送动作时，存在使用以树脂为原材料的树脂螺栓的情况。树脂螺栓虽然有各种各样的特征，但由于与金属螺栓相比强度低，适用范围被限制。因此无法应用于要求更高强度的领域。(日本)特开平7-293535号公报(专利文献1)中公开了为增强螺栓的拉伸破坏强度而混入纤维的树脂螺栓。在专利文献1中记载的树脂螺栓中，将平均纤维长度为0.3mm以上的长纤维混入热可塑性树脂，加强了强化纤维与树脂的结合力/粘着力，从而增强了复合材料的强度。现有技术文献专利文献专利文献1:(日本)特开平7-293535号公报
技术实现思路
专利文献1中记载的纤维强化树脂制螺栓通过努力使平均纤维长度0.3mm以上的长纤维与螺栓的轴向平行地取向来增强螺栓的拉伸破坏强度。然而，即使在含有长纤维而增强了轴向的拉伸强度的情况下，例如想要在稍小的空间内进行螺栓结合的情况下，想要缩短外螺纹与内螺纹的螺合长度时，存在螺纹牙强度...
【技术保护点】
一种纤维强化树脂螺栓，其使用树脂中含有强化纤维的树脂组合物而成型，所述纤维强化树脂螺栓的特征在于，所述纤维强化树脂螺栓中的螺纹牙的螺距是与公制粗牙螺纹、统一标准粗牙螺纹、统一标准细牙螺纹的标准所规定的所述螺纹牙外径对应的标准螺距的1.5倍至2倍长，所述强化纤维的平均纤维长度是所述纤维强化树脂螺栓中的螺纹牙的螺距的1至1/3倍，所述强化纤维的含有率是20％至80％。
【技术特征摘要】
【国外来华专利技术】2014.11.21 JP 2014-2365161.一种纤维强化树脂螺栓，其使用树脂中含有强化纤维的树脂组合物而成型，所述纤维强化树脂螺栓的特征在于，所述纤维强化树脂螺栓中的螺纹牙的螺距是与公制粗牙螺纹、统一标准粗牙螺纹、统一标准细牙螺纹的标准所规定的所述螺纹牙外径对应的标准螺距的1.5倍至2倍长，所述强化纤维的平均纤维长度是所述纤维强化树脂螺栓中的螺纹牙的螺距的1至1/3倍，所述强化纤维的含有率是20％至80％。2.如权利要求1所述的纤维强化树脂螺栓，其特征在于，所述纤维强化树脂螺栓中的螺纹牙的角度是60°至90°。3.如权利要求1所述的纤维强化树脂螺栓，其特征在于，所述纤维强化树脂螺栓的外径是3.5至10mm。4.如权利要求1所述的纤维强化树脂螺栓，其特征在于，所述树脂是芳香族聚醚酮树脂、聚酰胺树脂、聚酰亚胺树脂、聚苯硫醚树脂、聚偏氟乙烯树脂、聚碳酸酯树脂、聚缩醛树脂、酚醛树脂、超高分子量聚乙烯树脂、四氟乙烯－全氟烷基乙烯基醚树脂、聚对苯二甲酸丁二醇酯树脂或聚氯乙烯树脂。5.如权利要求1至4中任一项所述的纤维强...