The present invention provides a method for the manufacture of iron coke to produce high strength iron Coke without causing the fusion of the moldings to each other. In the process of producing iron coke by forming a mixture of coal and iron ore and by dry distillation, the refractory coal is used as a coal with an expansion number (CSN) below 2. As a preferred example, hard coal and coal softening easy coal mixed coal softening, softening and hard coal is the crucible swelling number (CSN) and 1 volatile components for more than 17% of coal, coal is easy to soften with easy to soften coal CSN and coal ratio in all the multiplication a value of 0.3 to 5.2 of the range of coal. In addition, as the preferred example, hard coal and coal softening coal mixed coal to softening, softening of hard coal is the crucible swelling number (CSN) for 1.5 ~ 2 of the coal, and coal is easy to soften with easy to soften coal and coal ratio in all CSN and value multiplication 5 of the range of coal.
【技术实现步骤摘要】
【国外来华专利技术】铁焦的制造方法
本专利技术涉及将煤和铁矿石的混合物干馏而得到的铁焦的制造方法。
技术介绍
近年来，从对地球环境的担心考虑，对高炉作业强烈要求提高炉内的还原反应，作为其中一环，将煤和铁矿石的混合物成型、干馏而得到的铁焦的使用备受关注。一般使用煤干馏中显示软化熔融性的易软化性煤(粘结煤、强粘结煤)或抑制成型物彼此的熔合的难软化性煤(非微粘结煤、非粘结煤)来制造上述铁焦。上述难软化性煤是在JISM8801所记述的吉塞勒塑性计(GieselerPlastometer)进行的测定中最高流动度小于2ddpm的煤。另外，对铁焦而言，重要的是反应性优异，然而在高炉内容易粉化则导致在高炉内的通气性的恶化，因此需要一定程度的强度。一般来说，大多情况下将煤与铁矿石的配合比率为7：3左右，如果铁矿石的比率在该值以下，则有铁焦的反应性降低的趋势，另一方面，即便在该值以上，也存在反应性的提高小、铁焦强度大幅降低的趋势。关于强度，例如，在独立行政法人新能源·产业技术总合开发机构自2006年度实施的“关于革新的炼铁工艺的研究”中，作为目标的铁焦转鼓强度(150转6mm指数)定义为82以上。以往，...
【技术保护点】
一种铁焦的制造方法，其特征在于，在将煤和铁矿石的混合物成型、干馏而制造铁焦的方法中，作为所述煤，使用坩埚膨胀序数CSN为2.0以下的难软化性煤。
【技术特征摘要】
【国外来华专利技术】2015.02.06 JP 2015-0216951.一种铁焦的制造方法，其特征在于，在将煤和铁矿石的混合物成型、干馏而制造铁焦的方法中，作为所述煤，使用坩埚膨胀序数CSN为2.0以下的难软化性煤。2.根据权利要求1所述的铁焦的制造方法，其特征在于，作为所述煤，使用坩埚膨胀序数CSN为1.5～2.0的难软化性煤。3.根据权利要求1所述的铁焦的制造方法，其特征在于，所述煤为难软化性煤和易软化性煤的混煤，并且该难软化性煤是坩...
【专利技术属性】
技术研发人员：藤本英和，庵屋敷孝思，塩沢亨，
申请(专利权)人：杰富意钢铁株式会社，
类型：发明
国别省市：日本,JP
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。