The present invention provides an inorganic coating which is calculated by mass percentage, consisting of 10~30% white cement, 0~20% black cement, 3~6% inorganic color powder, 60~70% tailings powder and residual additive. The invention also provides a method for preparing the inorganic coating, weighted according to the weight percentage of each reaction substance; the black, white cement, cement powder mixing tailings to enter a reaction vessel, 2 4 minutes after the addition of inorganic pigments and additives, and then stirring, mixing for packaging. The invention makes great use of different kinds of tailings materials in different regions so as to turn waste into treasure. At the same time, because the invention is dry powder, the water is added to the field construction to be modulated, so that the transportation cost is lowered during transportation. Moreover, due to the dry powder, the shelf life of the invention is quite long. The tailings powder and inorganic toner used are naturally formed and have good fastness to fading and weathering.
【技术实现步骤摘要】
一种无机涂料及其制备方法
：本专利技术属于化工领域，尤其涉及一种涂料，具体来说是一种无机涂料及其制备方法。
技术介绍
：矿产资源是国民经济重要的物质基础，随着工业化过程的加快，国民经济的发展对能源和原材料的需求越来越大。钢铁工业作为国民经济的支柱产业之一，尤其是正处于国民经济高速发展中的我国钢铁工业就显得更为重要。然而，随着矿山不断采深，矿石品位日趋下降，尾矿量和相应投资逐步增大，尾矿资源再生利用已成为矿业开发的一项主要内容。我国现有尾矿库四百多个，直接污染土地上百万亩，间接污染土地约一千万亩，每年运费高达75亿元。同时，矿山每天排出的大量尾矿，对环境造成了严重的污染。众所周知，尾矿具有粒度大小不等、数量大、可利用性高、价格便宜、处理成本低等特点，是宝贵的二次资源，应该很好地开发利用。所以，如果我们能对尾矿进行有效地二次综合利用，不仅可以减少尾矿的堆存，节约建坝、防洪等工程费用，改善对环境造成的污染，而且还能为国家创造财富，取得一定的经济、社会和环境效益。现有技术的涂料基本上都属于有机涂料，有机涂料添加有大量的有机物，有机物不易降解，耐候性差，使用寿命短，而且在生...
【技术保护点】
一种无机涂料，其特征在于：由以下质量百分比的成份组成：白水泥 10~30%、黑水泥 0~20%；无机色粉 3~6%；尾矿颗粒 60~70%；添加剂 余量。
【技术特征摘要】
1.一种无机涂料，其特征在于：由以下质量百分比的成份组成：白水泥10~30%、黑水泥0~20%；无机色粉3~6%；尾矿颗粒60~70%；添加剂余量。2.根据权利要求1所述的无机涂料，其特征在于：所述的添加剂为塑胶粉、纤维素、碱性中和剂、抗渗剂中的任意一种或者两种以上的组合。3.根据权利要求1所述的无机涂料，其特征在于：由以下质量百分比的成份组成：白水泥10~30%、黑水泥...
【专利技术属性】
技术研发人员：凌小平，
申请(专利权)人：上海同造欧式建筑科技有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。