多层积层基板制造技术
Multilayer substrate
The present invention provides a multilayer laminated substrate with low color change, beautiful appearance and good weather resistance and far infrared reflectivity. Multilayer laminate substrate of the invention at least comprises a transparent resin substrate, [A] metal oxide layer [C], conductive metal layer [D], high refractive index metal oxide layer [E], and containing inorganic oxides and inorganic nitrogen in at least one of the protective layer [F] layer sequentially piled up, and meet the following (1) and (2): (1) the protective layer [F] film thickness is 5nm ~ 300nm; (2) compared with the sum of metal elements, containing the protective layer of [F] semi metallic elements and semiconductor elements, containing the protective layer containing [F]% carbon is below 50%.
【技术实现步骤摘要】
【国外来华专利技术】
本专利技术涉及一种色调变化少、具有美观的外观、耐候性良好的远红外线反射性的多层积层基板。
技术介绍
以往，通过控制通过窗户等的红外线来降低调温或保冷所需要的能量的材料，公知的有：在透过可见光的基材上，层积由金、银和铜等组成的金属薄膜层，以及氧化钛、ITO和氧化锌等金属氧化物层组成的红外线反射层而成的薄膜(参照专利文献1和专利文献2)，或者玻璃等的多层积层体。这样的多层积层体具有使可见光通过和反射近红外线的特性。多层积层体充分利用该特性，被用于阻隔从建筑或交通工具的窗口处进入的太阳能量来提高空调效果，或者提高冷冻冷藏柜中的保冷效果等用途。另外，在上述专利文献1或专利文献2中，记载了利用聚甲基丙烯酸甲酯等丙烯酸类树脂、由硅酸乙酯得到的多聚物等硅树脂、聚酯树脂、三聚氰胺树脂以及氟树脂等构成的表面保护层作为物理性地保护红外线反射层的手段。另外，除上述表面保护层以外，由聚烯烃类树脂组成的表面保护层也已为公众所知。在先技术文献专利文献专利文献1：日本特公昭58-010228号公报专利文献2：日本特开2001-310407号公报
技术实现思路
专利技术欲解决的课题由具有良好耐划伤...
【技术保护点】
多层积层基板，至少由透明树脂基板[A]、金属氧化物层[C]、导电性金属层[D]、高折射率金属氧化物层[E]，以及含有无机氧化物和无机氮化物中的至少一者的保护层[F]按序层积而成，且满足以下(1)和(2)：(1)所述保护层[F]的膜厚为5nm～300nm；(2)相对于所述保护层[F]含有的金属元素、半金属元素及半导体元素的总和，所述保护层[F]含有的碳的含有质量％为50％以下。
【技术特征摘要】
【国外来华专利技术】2015.01.20 JP 2015-008304;2015.07.21 JP 2015-143701.多层积层基板，至少由透明树脂基板[A]、金属氧化物层[C]、导电性金属层[D]、高折射率金属氧化物层[E]，以及含有无机氧化物和无机氮化物中的至少一者的保护层[F]按序层积而成，且满足以下(1)和(2)：(1)所述保护层[F]的膜厚为5nm～300nm；(2)相对于所述保护层[F]含有的金属元素、半金属元素及半导体元素的总和，所述保护层[F]含有的碳的含有质量％为50％以下。2.根据权利要求1所述的多层积层基板，其特征在于：保护层[F]含有硅和碳，所述硅的至少一部分为氧化硅和/或氮化硅，且满足以下a和...
【专利技术属性】
技术研发人员：前田行弘，北川雅之，武田昌信，
申请(专利权)人：东丽株式会社，
类型：发明
国别省市：日本;JP