本发明专利技术低碳物质高效再生燃料，涉及含碳量低的物质如煤矸石、煤渣、泥煤、劣质煤、褐煤、风化煤、碳质页岩的回收利用，与环保、节能技术有关，将低碳物质配以重量5～10%的助剂，包括助燃剂，粘接疏松剂、氧化剂、催化剂、再生能源剂和水，加工成型煤，本发明专利技术产品与普通燃煤加工成的生活用型煤燃值相当，燃烧效果如点火易难度、可用火时间、最高火焰高度都比普通生活用型煤好。

Highly efficient renewable fuels for low carbon materials

Fuel efficient regeneration of the present invention relates to a low carbon material, low carbon material such as recycling of coal gangue, coal cinder, coal, coal, lignite and weathering coal, carbonaceous shale utilization, related to environmental protection, energy saving technology, low carbon material with a weight of 5 to 10% of the additives, including combustion agent, adhesive osteoporosis agent, oxidant, catalyst, renewable energy and water processing agent, coal, the product of the invention and ordinary coal processing into life with coal burning value, combustion effects such as difficulty, easy ignition time, the highest available fire flame height is greater than that of ordinary life with good coal.

【技术实现步骤摘要】

本专利技术涉及含碳量低的物质如煤矸石、煤渣、泥煤、劣质煤、褐煤、风化煤、碳质页岩的回收利用，与环保、节能技术有关，具体地说，是一种低碳物质高效再生燃料。
技术介绍
：一些低碳含量的物质如煤矸石，含碳量约为12～25%，其燃值按碳测定一般为800～2000卡/g，如果这些含碳量低的物质如煤矸石制成型煤，通常都要添加20～30%的粘合剂如黄泥、石炭等，因而使本来含碳量低的物质的碳含量变得更低，除影响型煤的燃值外，还存在难点燃，烟雾大等缺点，因而用传统方法生产煤矸石型煤，用作民用生活用煤，老百姓都称之为伪劣产品，为了提高煤矸石或其他低碳含量物质的碳含量，提高热值，通常的办法是在煤矸石中加入多量的煤或木炭，再按传统的方法加工型煤，通常的加入量至少要20～30%，如《煤矸石燃料的配制方法》，申请号88106225，煤矸石中就配煤20～30%。本专利技术专利技术人在长期型煤生产中发现，一般的煤炭中碳含量为60～75%，燃值4000～6000卡/g，通常型煤生产都要加入40～50%的黄泥作粘合剂，这样加工而成的型煤其中碳含量实际为40～50%，已接近煤矸石中的碳含量，也就本文档来自技高网...

【技术保护点】
一种低碳物质高效再生燃料，其特征是由煤矸石1吨和其他助剂木炭40～50kg，粘接疏松剂甲基纤维素2～3kg，氧化剂硝酸钾15kg，催化剂苯甲酸2kg，再生燃源剂金属硫化物如FeS 30～40kg配制加水，加工而成的型煤。

【技术特征摘要】
1.一种低碳物质高效再生燃料，其特征是由煤矸石1吨和其他助剂木炭40～50kg，粘接疏松剂甲基纤维素2～3kg，氧化剂硝酸钾15kg，催化剂苯甲酸2kg，再生燃源剂金属硫化物如FeS30～40kg配制加水，加工而成的型煤。
2.根据权利要求1所述的一种低碳物质高效再生燃料，其特征是所指低碳物质包括煤渣、泥煤、劣质煤、褐煤...