The invention belongs to the field of electrochemistry, which discloses a graphene and its preparation method, electrode and super capacitor; the preparation method comprises the following steps: graphene preparation of graphene oxide suspension; condensed solution preparation containing graphene oxide; graphene oxide solution preparation of nitrogen doped the preparation of graphene. Graphene prepared by the method of the invention can obtain high surface area, high conductivity of graphene. The graphene prepared by super capacitor can improve the energy density and power density of the capacitor; the method of one step to achieve a variety of properties of the Shi Moxi material, simplifies operation steps, greatly reducing the cost of production.
【技术实现步骤摘要】
本专利技术涉及电化学领域，尤其涉及一种石墨烯及其制备方法。本专利技术还涉及使用石墨烯为活性材料的电极片，以及使用该电极片的超级电容器。
技术介绍
超级电容器(Supercapacitors)又称电化学电容器(ElectrochemicalCapacitors)或者双电层电容器(ElectricDoubleLayerCapacitors)，它是一种介于传统电容器和电池之间的新型储能元件，与传统电容器相比具有更高比电容量和能量密度，与电池相比则具有更高的功率密度；由于超级电容器具有充放电速度快、对环境无污染和循环寿命长等优点，有希望成为本世纪新型的绿色能源。电极材料是超级电容器的重要组成部分，是影响超级电容器电容性能和生产成本的关键因素，因此研究开发高性能、低成本的电极材料是超级电容器研究工作的重要内容。目前研究的超级电容器的电极材料主要有炭材料、金属氧化物及其水合物电极材料和导电聚合物电极材料。目前双电层超级电容器的电极材料主要为碳材料，具有优良的导热和导电
【技术保护点】
一种石墨烯的制备方法，其特征在于，包括如下步骤：将氧化石墨加入到水中超声分散处理，得到浓度为1～20mg/ml的氧化石墨烯悬浮液；将浓度为1～500g/L的KOH溶液加入到所述氧化石墨烯悬浮液中，搅拌，得到凝聚状溶液；将浓度为1～500g/L的NaOH溶液加入到所述凝聚状溶液中，充分搅拌1～5h，得到混合溶液；将上述得到混合溶液过滤，并将滤物进行干燥处理，再将干燥后的滤物放入马弗炉中并于惰性氛围下进行高温煅烧，冷却后、水洗、过滤、干燥，得到所述石墨烯。
【技术特征摘要】
1.一种石墨烯的制备方法，其特征在于，包括如下步骤：
将氧化石墨加入到水中超声分散处理，得到浓度为1～20mg/ml的氧化
石墨烯悬浮液；
将浓度为1～500g/L的KOH溶液加入到所述氧化石墨烯悬浮液中，搅
拌，得到凝聚状溶液；
将浓度为1～500g/L的NaOH溶液加入到所述凝聚状溶液中，充分搅拌
1～5h，得到混合溶液；
将上述得到混合溶液过滤，并将滤物进行干燥处理，再将干燥后的滤
物放入马弗炉中并于惰性氛围下进行高温煅烧，冷却后、水洗、过滤、干
燥，得到所述石墨烯。
2.根据权利要求1所述的石墨烯的制备方法，其特征在于，所述超
声分散处理时间为1～5h。
3.根据权利要求1所述的石墨烯的制备方法，其特征在于，所述凝
聚状溶液中，KOH与氧化石墨烯的质量比为1～30∶1。
4.根据权利要求1所述的石...