本发明专利技术公开了一种纺织品及其生产方法，该纺织品中至少30重量%以上的纱线为具有如下特征的复合纱，复合纱中饰纱为预取向丝、芯纱为全牵伸丝，饰纱与芯纱的丝长差为1.0%～35%、芯纱与饰纱的L值差在5以上，其中饰纱的结晶度为45%～65%、晶格尺寸在30nm以上、断裂伸长率在45%以上；且复合纱的捻度为400～3500T/M；在染色后整理加工过程中，不需经过特殊的后加工即可得到手感柔软、蓬松性好，悬垂性优良的纺织品。

Textile and production method thereof

The invention discloses a textile and its production method, at least 30 wt% of yarn for composite yarn has the following characteristics in the textile, composite yarn and yarn for pre oriented yarn, core spun yarn for FDY, yarn and yarn yarn length difference is 1% ~ 35%, core spun yarn and decoration yarn L value difference is above 5, the yarn crystallization degree is 45% ~ 65%, the lattice size is above 30nm, the elongation is above 45%; and the composite yarn twist is 400 ~ 3500T/M; finishing in the dyeing process, without special processing can be soft and fluffy. Good drapability excellent textile.

【技术实现步骤摘要】

本专利技术涉及一种纺织品及其生产方法。
技术介绍
现在市场上具有一定丝长差、手感柔软蓬松的化纤长丝纺织品，其一般采用高超喂率的塔丝隆纱线，塔丝隆纱线在表面形成类似短纤触感的线圈，由于其在加工过程中采用高的超喂率，加工的稳定性差，并且复合纱线在退解过程中，由于丝圈间相互缠结，往往容易造成退解性困难的问题；在作为经纱用途时，整经、上浆以及织造过程中，塔丝隆纱线的线圈在钢筘中的通过性差，容易产生断头现象，严重降低了生产效率。并且塔丝隆纱线在加工过程中，为了得到很好的交缠效果，往往采用高的加工压力和低的加工速度，这样大大增加了加工成本。另外，塔丝隆纱线在使用工程中，往往直接使用或加弱捻，这样生产的纺织品，悬垂性比较差，只能作为运动服、休闲服等一般用途，不能满足高级时装面料悬垂性等的要求。再者，塔丝隆复合纱线的芯部和饰部均采用的FDY,这样所制备成的纺织品，手感一般都比较干燥。中国专利CN02132202.3“复合变形纱，其制造方法，用该复合变形丝纱制作的机织织物或针织织物，以及用于生产该变形纱的设备”中，所采用的芯纱和饰纱是被假捻和卷曲的，虽然芯纱在热处理条本文档来自技高网...

【技术保护点】
一种纺织品，其特征是：该纺织品至少30重量%以上的纱线为具有如下特征的复合纱，所述复合纱中饰纱为预取向丝、芯纱为全牵伸丝，饰纱与芯纱的丝长差为1.0%～35%、芯纱与饰纱的L值差在5以上，其中饰纱的结晶度为45%～65%、晶格尺寸在30nm以上、断裂伸长率在45%以上；且所述复合纱的捻度为400～3500T/M。

【技术特征摘要】
1.一种纺织品，其特征是：该纺织品至少30重量%以上的纱线为具有如下特征的复合纱，所述复合纱中饰纱为预取向丝、芯纱为全牵伸丝，饰纱与芯纱的丝长差为1.0%～35%、芯纱与饰纱的L值差在5以上，其中饰纱的结晶度为45%～65%、晶格尺寸在30nm以上、断裂伸长率在45%以上；且所述复合纱的捻度为400～3500T/M。
2.根据权利要求1所述的纺织品，其特征是：所述芯纱或饰纱的纤维原料为聚酯纤维或聚酰胺纤维。
3.一种权利要求1所述的纺织品的生产方法，其特征是：选用预取向丝作为饰纱、全牵伸丝作为芯纱，其中饰纱经过驰缓热处理后，与芯纱在交络喷嘴处进行复合形成纤度为30～120旦尼尔的...