The invention belongs to the field of graphene, which discloses a method for preparing graphene, comprising the steps of: graphite oxide added to the solvent, ultrasonic, obtained the graphene oxide suspension; the crude product of graphene oxide suspension sealed under heat and pressure treatment and obtained after washing, filtering, drying. Graphene. Method for preparing graphene provided by the invention, the exfoliated graphene oxide suspension liquid ultrasonic, through the use of high temperature and high pressure reaction kettle, decomposition of functional groups on the graphene oxide, to achieve reduction, and then through the instant release of pressure, the sudden release of high-pressure hot steam, produce a larger force between the layers of graphene, prevent aggregation, and obtain a high ratio of surface area of graphene.
【技术实现步骤摘要】
本专利技术涉及石墨烯领域，尤其涉及一种石墨烯的制备方法。
技术介绍
自从英国曼彻斯特大学的安德烈·K·海姆(AndreK.Geim)等在2004年制备出石墨烯材料，由于其独特的结构和光电性质受到了人们广泛的重视。单层石墨由于其大的比表面积，优良的导电、导热性能和低的热膨胀系数而被认为是理想的材料。如：①高强度，杨氏摩尔量，(1,100GPa)，断裂强度：(125GPa)；②高热导率，(5,000W/mK)；③高导电性、载流子传输率，(200,000cm2/V·s)；④高的比表面积，(理论计算值：2,630m2/g)。尤其是其高导电性质，大的比表面性质和其单分子层二维的纳米尺度的结构性质，可在超级电容器和锂离子电池中用作电极材料。到目前为止，氧化还原法是一种大量制备石墨烯的方法。而氧化石墨在还原成石墨烯的过程中，很容易团聚，导致表面积降低。通过将氧化石墨从室温直接移入1000℃的环境中，进入加热处理，所制备的石墨烯会存在一点的缺陷，导致电导率低。通过缓慢加热的方...
【技术保护点】
一种石墨烯的制备方法，其特征在于，包括如下步骤：氧化石墨烯悬浮液的制备：将氧化石墨加入溶剂中，配置成浓度为0.25‑1mg/ml的氧化石墨溶液，并对氧化石墨溶液超声处理，得到均匀分散的氧化石墨烯悬浮液；石墨烯悬浮液：将所述氧化石墨烯悬浮液中放入反应釜中后进行密封，然后对反应釜加热、加压处理，得到石墨烯初产品，将此石墨烯初产品用乙醇反复冲洗，过滤，干燥，得到石墨烯。
【技术特征摘要】
1.一种石墨烯的制备方法，其特征在于，包括如下步骤：
氧化石墨烯悬浮液的制备：将氧化石墨加入溶剂中，配置成浓度为
0.25-1mg/ml的氧化石墨溶液，并对氧化石墨溶液超声处理，得到均匀分散
的氧化石墨烯悬浮液；
石墨烯悬浮液：将所述氧化石墨烯悬浮液中放入反应釜中后进行密
封，然后对反应釜加热、加压处理，得到石墨烯初产品，将此石墨烯初产
品用乙醇反复冲洗，过滤，干燥，得到石墨烯。
2.根据权利要求1所述的石墨烯的制备方法，其特征在于，所述氧
化石墨溶液配制中所用的溶剂为水、异丙醇、乙醇及...
【专利技术属性】
技术研发人员：周明杰，吴凤，王要兵，袁新生，
申请(专利权)人：海洋王照明科技股份有限公司，深圳市海洋王照明技术有限公司，深圳市海洋王照明工程有限公司，
类型：发明
国别省市：广东;44