多异氰酸酯组合物、涂料组合物及涂装体的制造方法技术

一种多异氰酸酯组合物、涂料组合物及涂装体的制造方法。提供表现出高的干燥性、进而具有湿气稳定性和与多元醇的相容性优异的性能的多异氰酸酯组合物和含有其的涂料组合物以及涂装方法。一种多异氰酸酯组合物，其为由选自脂肪族二异氰酸酯和脂环族二异氰酸酯中的一种以上的二异氰酸酯和一种以上的二元醇得到的多异氰酸酯组合物，前述多异氰酸酯组合物中，脲基/(脲基+异氰脲酸酯基)的摩尔比为0.0001～0.1、并且脲基甲酸酯基/(异氰脲酸酯基+脲基甲酸酯基)的摩尔比为0.2～0.9。

Polyisocyanate composition, coating composition and process for producing coating

Polyisocyanate composition, coating composition and process for producing coating. Polyisocyanate compositions exhibiting excellent drying properties, thereby having moisture stability, and excellent compatibility with polyols, and coating compositions containing the same, and methods of coating. A polyisocyanate composition, polyisocyanate composition for selected from aliphatic diisocyanate and alicyclic diisocyanate in more than one diisocyanate and a diol obtained above, the polyisocyanate composition, urea / (urea + isocyanurate) molar ratio of 0.0001 to 0.1, and urea formic acid ester / (isocyanurate group + allophanate based) molar ratio of 0.2 to 0.9.

【技术实现步骤摘要】
多异氰酸酯组合物、涂料组合物及涂装体的制造方法
本专利技术涉及多异氰酸酯组合物、涂料组合物及涂装体的制造方法。
技术介绍
已知以往聚氨酯树脂涂料作为具有优异的耐磨耗性、耐化学性、耐污染性的涂料，特别是使用由六亚甲基二异氰酸酯、异佛尔酮二异氰酸酯衍生得到的无黄变多异氰酸酯的聚氨酯树脂涂料具有进一步优异的耐候性。因此，这种多异氰酸酯的使用，以常温或热固化的双组分氨基甲酸酯涂料的形态涉及建筑、重防、汽车、工业用及其修补等多方面。各使用中，为了缩短工序等，期待提高固化性。为了提高固化性，例如存在添加有机锡化合物等的方法，但是该方法存在下述问题：根据涂料的组合物不同而效果有可能不同、在涂装等中挥发的有机溶剂对处理装置的燃烧催化剂造成不良影响等。另一方面，为了解决这些问题，高官能性多异氰酸酯的开发得到进展。专利文献1中提出了，通过至少一种脂肪族或脂环族二异氰酸酯与多官能性醇的反应后的异氰脲酸酯化，或者通过上述醇存在下的异氰脲酸酯化，得到高官能性多异氰酸酯。现有技术文献专利文献专利文献1：日本特开平6-312969号公报
技术实现思路
专利技术要解决的问题将多异氰酸酯与主剂混合来使用时，必要量为少量的本文档来自技高网...

【技术保护点】
一种多异氰酸酯组合物，其为由选自脂肪族二异氰酸酯和脂环族二异氰酸酯中的一种以上的二异氰酸酯和一种以上的二元醇得到的多异氰酸酯组合物，所述多异氰酸酯组合物中，脲基/(脲基+异氰脲酸酯基)的摩尔比为0.0001～0.1、并且脲基甲酸酯基/(异氰脲酸酯基+脲基甲酸酯基)的摩尔比为0.2～0.9。

【技术特征摘要】
2016.03.14 JP 2016-0498161.一种多异氰酸酯组合物，其为由选自脂肪族二异氰酸酯和脂环族二异氰酸酯中的一种以上的二异氰酸酯和一种以上的二元醇得到的多异氰酸酯组合物，所述多异氰酸酯组合物中，脲基/(脲基+异氰脲酸酯基)的摩尔比为0.0001～0.1、并且脲基甲酸酯基/(异氰脲酸酯基+脲基甲酸酯基)的摩尔比为0.2～0.9。2.根据权利要求1所述的多异氰酸酯组合物，其中，脲基甲酸酯基/(脲基甲酸酯基+氨基甲酸酯基)的...

【专利技术属性】
技术研发人员：福地崇史，洪昌峰，
申请(专利权)人：旭化成株式会社，
类型：发明
国别省市：日本,JP