An improved olive disclosed green transparent glaze, characterized by the following components: the weight fraction of Jiepai mud 20 ~ 22, 3 ~ 10 mica, Suzhou soil from 4 to 7, 15 to 17 portions of wash mud, 11 to 13 portions of talcum powder, quartz powder 13 to 15, 3 to 5 parts of sodium humate, porcelain powder 9 ~ 11, 5 ~ 7 ballstone, bentonite 12 ~ 14, 6 ~ 8 aluminum powder, 60 to 68 portions of each flux; the weight fraction of the flux consists of the following components: Malachite 28 ~ 33, 18 kaolin ~ 21, borax 20 to 22, 9 to 11 portions of feldspar, limestone from 5 to 7, 0.5 to 2.5 portions of tourmaline. The invention adopts the improved olive green transparent glaze fired porcelain high transparency, crisp sound, good color and luster, smooth and stable atmosphere.
【技术实现步骤摘要】
一种改进型橄榄绿透明釉料
本专利技术涉及釉料制备
,特别涉及一种改进型橄榄绿透明釉料。
技术介绍
透明釉是指通过釉层可以看见釉下坯体的颜色以及各种雕刻和彩饰的釉,分为无色和着色清沏透明的釉。透明釉的种类较多，如日用瓷和卫生瓷上用的石灰釉、长石釉以及釉面砖上使用的铅硼釉等。但是目前的透明釉存在着烧制出来的瓷器存在透明度不高，声音不清脆的问题。另外,橄榄绿色给人以规整端庄之感，应用于陶瓷上能形成独特的美感，显得大气磅礴。多年来，人们试图烧制出稳定的橄榄绿色陶瓷产品，但成功率较低，因此，研发出稳定的橄榄绿色透明釉料成为一重大难题。
技术实现思路
本专利技术所要解决的技术问题在于针对现有透明釉所存在上述技术问题而提供一种烧制出来的瓷器透明度高，声音清脆的改进型橄榄绿透明釉料。本专利技术所要解决的技术问题可以通过以下技术方案来实现：一种改进型橄榄绿透明釉料，由以下重量分数的各组分组成：界牌泥20～22份，云母3～10份，苏州土4～7份，洗泥15～17份，滑石粉11～13份，石英粉13～15份，腐植酸钠3～5份，瓷粉9～11份，球石5～7份，膨润土12～14份，铝粉6～8份...
【技术保护点】
一种改进型橄榄绿透明釉料，其特征在于，由以下重量分数的各组分组成：界牌泥20～22份，云母3～10份，苏州土4～7份，洗泥15～17份，滑石粉11～13份，石英粉13～15份，腐植酸钠3～5份，瓷粉9～11份，球石5～7份，膨润土12～14份，铝粉6～8份,熔剂60～68份；所述熔剂由以下重量分数的各组分组成：孔雀石28～33份，高岭土18～21份，硼砂20～22份，长石9～11份，石灰石5～7份，电气石0.5～2.5份。
【技术特征摘要】
1.一种改进型橄榄绿透明釉料，其特征在于，由以下重量分数的各组分组成：界牌泥20～22份，云母3～10份，苏州土4～7份，洗泥15～17份，滑石粉11～13份，石英粉13～15份，腐植酸钠3～5份，瓷粉9～11份，球石5～7份，膨润土12～14份，铝粉6～8份,熔剂60～68份；所述熔剂由以下重量分数的各组分组成：孔雀石28～33份，高岭土18～21份，硼砂20～22份，长石9～11份，石灰石5～7份，电气石0.5～...
【专利技术属性】
技术研发人员：谭海燕，
申请(专利权)人：衡东县东康瓷业有限公司，
类型：发明
国别省市：湖南,43