The invention relates to a fireproof paint, including water glass, silicone resin, calcium carbonate, asbestos, formaldehyde absorbent, thickening agent, water quality, the number of copies of each component is 12 water glass 27, 10 silicone resin 18, calcium carbonate 15 30, 10, 6 asbestos formaldehyde absorption collector 8 10, 10 thickener 20, water 30 50. Fireproof paint of the invention is not containing cobalt, lead, used alone, painted light color, good quality, low temperature resistance, high humidity and other characteristics; apply to all kinds of material surface, quick drying, no sagging, blistering, film formation, has excellent physical and chemical properties, protection, good decorative function the material of play.
【技术实现步骤摘要】
一种防火漆
本专利技术涉及一种家装涂料领域，具体地讲，本专利技术涉及一种防火漆。
技术介绍
普遍存在的油性涂料主要是使用含有大量有毒有害物质的香蕉水、天拿水作为稀释剂，无与伦比的环保优势是水性涂料最大的特点。目前国内外正大力发展水性涂料，随着人们对防火漆要求的提高，近年来急需在防火漆生产方法改进上有突破。
技术实现思路
针对现有技术中存在的上述不足，本专利技术所要解决的技术问题是提供一种效果好的防火漆。本专利技术解决其技术问题所采用的技术方案是：提供一种防火漆，包括水玻璃、有机硅树脂、重质碳酸钙、石棉、甲醛吸收剂、增稠剂、水，各组分的质量份数为：水玻璃12-27、有机硅树脂10-18、重质碳酸钙15-30、石棉6-10、甲醛吸收剂8-10、增稠剂10-20、水30-50。作为优选，所述防火漆各组分的质量份数为：水玻璃23、有机硅树脂15、重质碳酸钙22、石棉7、甲醛吸收剂8、增稠剂20、水50。作为优选，所述水玻璃固含量为23-50wt%。作为优选，所述增稠剂为聚丙烯酸酯和聚氨酯的混合物。作为优选，所述水为去离子水。作为优选，所述防火漆的制备方法，其特征在于包括下述步骤：1)将水玻璃加入搅拌缸中，加入有机硅树脂、重质碳酸钙，搅拌均匀；2)向搅拌缸均匀加入石棉，高速搅拌分散；3)均匀加入甲醛吸收剂、增稠剂，搅拌均匀；4)倒入所给质量份数的水，加热20分钟；5)过滤，滤液静置，即可。本专利技术的防火漆不含钴、铅，单独使用，有漆色浅、质量佳、耐低温、抗高湿等特点；涂于各种建筑表面，干燥迅速、不流挂、不起泡，漆膜平整、具有优异的理化性能，对建筑材质起到很好的保护、装饰...
【技术保护点】
一种防火漆，其特征在于：包括水玻璃、有机硅树脂、重质碳酸钙、石棉、甲醛吸收剂、增稠剂、水，各组分的质量份数为：水玻璃12‑27、有机硅树脂10‑18、重质碳酸钙15‑30、石棉6‑10、甲醛吸收剂8‑10、增稠剂10‑20、水30‑50。
【技术特征摘要】
1.一种防火漆，其特征在于：包括水玻璃、有机硅树脂、重质碳酸钙、石棉、甲醛吸收剂、增稠剂、水，各组分的质量份数为：水玻璃12-27、有机硅树脂10-18、重质碳酸钙15-30、石棉6-10、甲醛吸收剂8-10、增稠剂10-20、水30-50。2.根据权利要求1所述的防火漆，其特征在于：所述防火漆各组分的质量份数为：水玻璃23、有机硅树脂15、重质碳酸钙22、石棉7、甲醛吸收剂8、增稠剂20、水50。3.根据权利要求2所述的防火漆，其特征在于：所述水玻璃固含量...