The invention discloses a low temperature brittleness of PVC pipe, A, the measurement of PVC, stabilizer, nano calcium carbonate, APAO, filler, plasticizer, lubricant, titanium pigment, filler, antioxidant and whitening agent in cold mixed in a high-speed mixer: B, and then the mixture is cooled cold mixer 45 to 30 DEG C; C, then cooling the material into the plastic machine, for the first time, the first time D plasticization; plasticizing good raw materials adding traction machine; E, the traction after the material added to plastic machine, two times, two times the plasticization; F plasticized material join in the two traction traction machine. The anti low temperature brittleness PVC pipe and the manufacturing method thereof have the advantages of good shock resistance, cold resistance, good weather resistance, and low temperature brittleness of the PVC pipe prepared.
【技术实现步骤摘要】
一种抗低温脆性PVC管材及其制造方法
本专利技术属于PVC管材制造
，具体涉及一种抗低温脆性PVC管材及其制造方法。
技术介绍
塑料管材是高科技复合而成的化学建材，而化学建材是继钢材、木材、水泥之后，当代新兴的第四大类新型建筑材料。近年来，化学建材在我国取得了长足进步迅猛发展，尤其是新型环保塑料管材的广泛使用，掀起了一次代传统建材的革命。塑料管材因具有水流损失小、节能、节材、保护生态、竣工便捷等优点，目前广泛应用于建筑给排水、城镇给排水以及燃气管等领域，成为新世纪城建管网的主力军。聚氯乙烯(PVC)是世界上仅次于聚乙烯的第二大塑料品种，具有良好的机械和物理性能，由其制成的PVC管材因自重轻，具有良好的机械和物理性能，由其制成的PVC管材因耐腐蚀，耐压强度高，安全方便等特点得到了广泛应用，目前约70％的PVC管材用于排水/给水等建筑领域，但PVC管最大的缺陷就是耐寒性和低温抗冲击性能较差，使用温度下限约－15℃，极大限制了PVC管的使用,例如PVC管材在中国北方使用时，冬天极易发生脆裂，而且现有的抗低温脆性PVC管材都多只能够抗低温脆性，不能够抗氧化，而且生产...
【技术保护点】
一种抗低温脆性PVC管材，其特征在于：按重量份计，包括PVC 90‑100重量份、稳定剂2‑8重量份、纳米碳酸钙8‑10重量份、APAO 5‑10重量份、填充剂7‑8重量份、增韧剂20‑30重量份、钛白粉1‑3重量份、润滑剂0.5‑1.5重量份、填充剂7‑8重量份、抗氧剂0.1‑0.5重量份和增白剂2‑5重量份。
【技术特征摘要】
1.一种抗低温脆性PVC管材，其特征在于：按重量份计，包括PVC90-100重量份、稳定剂2-8重量份、纳米碳酸钙8-10重量份、APAO5-10重量份、填充剂7-8重量份、增韧剂20-30重量份、钛白粉1-3重量份、润滑剂0.5-1.5重量份、填充剂7-8重量份、抗氧剂0.1-0.5重量份和增白剂2-5重量份。2.根据权利要求1所述的一种抗低温脆性PVC管材，其特征在于：所述稳定剂为钙锌复合稳定剂。3.根据权利要求1所述的一种抗低温脆性PVC管材，其特征在于：所述PVC为通用型PVC、高聚合度PVC树脂和交联PVC树脂。4.根据权利要求1所述的一种抗低温脆性PVC管材，其特征在于：所述APAO选自均聚APAO和共聚APA...
【专利技术属性】
技术研发人员：杨俊斌，
申请(专利权)人：合肥科源塑胶有限公司，
类型：发明
国别省市：安徽,34