一种提升钛酸锂电导率的方法及钛酸锂技术
Method for improving conductivity of lithium titanate and lithium titanate
The invention belongs to the technical field of lithium ion battery materials, and discloses a method for improving the conductivity of lithium titanate, including: preparation of carbon coated TiO2; the carbon coated TiO2 and Li2CO3 dispersed in ethanol milling mixed; the mixture is milled for charging dry heat treatment at high temperature under inert gas atmosphere Li4Ti5O12/C, composite material; the processing conditions of the heat treatment temperature is 800 DEG C, 12h. The present invention provides a method for improving the conductivity of lithium titanate powder, to small particle size, uniform morphology, particles of high regularity, has high specific capacity and cycle life effect, can be used in the field of high power battery.
【技术实现步骤摘要】
一种提升钛酸锂电导率的方法及钛酸锂
本专利技术涉及锂离子电池纳米材料
，特别涉及一种提升钛酸锂电导率的方法及钛酸锂。
技术介绍
Li4Ti5O12因较碳材料负极具有高度安全性和稳定性，成为了安全型锂离子电池负极中广受关注的备选材料。作为负极材料，Li4Ti5O12具有稳定的放电电压平台(1.55VvsLi+/Li)且充放电过程中体积几乎不发生任何变化，具有“零应变”特性，因此具有非常好的循环性能。但Li4Ti5O12电子电导率低，大倍率充放电性能差。为提高Li4Ti5O12的电导率和电化学性能，现有技术中主要是通过颗粒纳米化、元素掺杂、引入导电相三种方法来增大电导率以提高大电流充放电性能。采用碳包覆对Li4Ti5O12进行碳复合改性，已被应用于工业生产当中；但是，合成的C/Li4Ti5O12样品电化学性能并不理想，难以达到高倍率动力电池领域的使用需求。
技术实现思路
本专利技术提供一种提升钛酸锂电导率的方法，达到粉末颗粒尺寸小，形貌均一，颗粒规整度高，具有较高的比容量和循环寿命的效果，可用于高倍率动力电池领域。为解决上述技术问题，本专利技术提供了一种提升钛酸锂电...
【技术保护点】
一种提升钛酸锂电导率的方法，其特征在于，包括：制备碳包覆TiO2；将所述碳包覆TiO2和Li2CO3分散在无水乙醇中球磨混合；将球磨后的混合料进行装料干燥，在惰性气体气氛下高温热处理，得到Li4Ti5O12/C复合材料；其中，所述高温热处理的处理条件为800℃，保持12h。
【技术特征摘要】
1.一种提升钛酸锂电导率的方法，其特征在于，包括：制备碳包覆TiO2；将所述碳包覆TiO2和Li2CO3分散在无水乙醇中球磨混合；将球磨后的混合料进行装料干燥，在惰性气体气氛下高温热处理，得到Li4Ti5O12/C复合材料；其中，所述高温热处理的处理条件为800℃，保持12h。2.如权利要求1所述的提升钛酸锂电导率的方法，其特征在于，所述制备碳包覆TiO2包括：将TiO2纳米粉和葡萄糖溶于乙醇中，室温搅拌；在集热搅拌容器中，快速升温搅拌蒸干溶剂得到干燥混合物；将所述干燥混合物以2～8℃/min升温到至少500℃，并在惰性气体气氛下锻烧，得到碳包覆TiO2。3.如权利要求2所述的提升钛酸锂电导率的方法，其特征在于，在所述集热搅拌容器中，蒸干溶剂过程温度保持在100℃。4.如权利要求2所述的提升钛酸锂...
【专利技术属性】
技术研发人员：曹元成，程琦，汤舜，闫继，梁济元，
申请(专利权)人：江汉大学，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。