The invention provides a core-shell acrylate emulsion and preparation method thereof, wherein the core-shell acrylic emulsion is prepared by semi continuous process system, the core of mixed monomer and shell monomer were mixed acrylic monomers containing specific content, core-shell acrylic emulsion was prepared with membrane temperature and the right to lower the lowest viscosity, good stability. Then, the ultra low VOC environmental protection waterborne high gloss finish paint is prepared by using the core-shell acrylic emulsion, which not only has high gloss, but also has ultra-low VOC content, and can satisfy people's various demands.
【技术实现步骤摘要】
核壳型丙烯酸乳液和超低VOC环保水性高光面漆及其制备方法
本专利技术涉及化工涂料领域，尤其涉及水性漆领域，具体涉及一种核壳型丙烯酸乳液和超低VOC环保水性高光面漆及其制备方法。
技术介绍
涂料主要用于物品的涂刷，其主要功能是装饰和保护作用，使物品美观整洁，能让我们感受到美感。近年来，人们对环保的要求越来越高，尤其在家庭装饰品方面，对涂料的各项性能具有更高的要求，除了具有涂层高光泽、高丰满度、高硬度、耐水、酸、碱性好的优点外，对VOC的低产生及低排放也有了更高的要求。现在我国大部分零售面漆存在高VOC的特点，对人体危害程度大，尤其是在人类活动密集的区域。如若降低VOC排放，会使体系相容性不佳，导致光泽低，装饰性差，其他各项性能下降。因此需要提供一种新的具有超低VOC，而且还保持有高光泽的环保水性面漆来满足人们的需求。
技术实现思路
针对上述问题，本专利技术的一方面提供了一种核壳型丙烯酸乳液，核和壳均由混合单体聚合形成，其中，按质量计，所述核壳型丙烯酸乳液的核混合单体中含有2-6％丙烯酸，壳混合单体中含有1-4％丙烯酸。进一步，所述壳混合单体与核混合单体的质量比为0.5-...
【技术保护点】
一种核壳型丙烯酸乳液，核和壳均由混合单体聚合形成，其特征在于：按质量计，核混合单体中含有2‑6％丙烯酸，壳混合单体中含有1‑4％丙烯酸。
【技术特征摘要】
1.一种核壳型丙烯酸乳液，核和壳均由混合单体聚合形成，其特征在于：按质量计，核混合单体中含有2-6％丙烯酸，壳混合单体中含有1-4％丙烯酸。2.根据权利要求1所述的核壳型丙烯酸乳液，其特征在于：所述壳混合单体与所述核混合单体的质量比为0.5-2:1。3.根据权利要求1所述的核壳型丙烯酸乳液，其特征在于：按质量计，所述核混合单体由2-6％丙烯酸、15-25％甲基丙烯酸羟乙酯、15-25％丙烯酸丁酯和45-65％甲基丙烯酸丁酯组成，所述壳混合单体由1-4％丙烯酸、20-40％甲基丙烯酸甲酯、40-60％丙烯酸丁酯和15-25％丙烯酸羟乙酯组成。4.根据权利要求1-3任一项所述的核壳型丙烯酸乳液的制备方法，其特征在于：所述制备方法为半连续加工工艺，包括以下步骤，将核混合单体逐滴滴入到含有第一引发剂和乳化剂的水溶液中；和将壳混合单体直接加入含有核聚合物乳液和第二引发剂的水溶液中。5.一种超低VOC环保水性高光面漆，包括A组分和B组分，其特征在于：所述A组分包含有权利要求1-3任一项所述的核壳型丙烯酸乳液，所述B组分为固化剂。6.根据权利要求5所述的超低VOC环保水性高光面漆，其特征在于：按质量份计，4-6份A组分与1份B组分配套使用。7.根据权利要求5所述的超低VOC环保水性高光面漆，其特征在于：所述固化剂由异氰酸酯和水组成。8.根据权利要...
【专利技术属性】
技术研发人员：刘胜普，
申请(专利权)人：河北晨阳工贸集团有限公司，
类型：发明
国别省市：河北,13