一种无需缓凝剂的高耐水性磷酸镁水泥制造技术

本发明专利技术属于磷酸镁水泥的制备领域，具体公开了一种无需缓凝剂的高耐水性磷酸镁水泥及其制备方法，主要原材料为镁粉，磷酸氢二盐和硅灰。制备步骤如下：将烧结氧化镁与硅灰混合并搅拌均匀，加入已事先溶于水的磷酸氢二盐溶液得到无需缓凝剂的高耐水性磷酸镁水泥。本发明专利技术具有高强度（28d抗压强度不低于100MPa），凝结时间较长（初凝时间不低于30min），耐水性好（56d强度保留率可达到95%以上）的特点。

A high water resistant magnesium phosphate cement without retarders

The invention belongs to the field of preparation of magnesium phosphate cement, in particular discloses a retarder without high water resistance of magnesium phosphate cement and its preparing method, the main raw material for magnesium hydrogen phosphate salt and silica fume, two. The preparation steps are as follows: mixing the sintered Magnesium Oxide with silica fume and mixing evenly, adding two hydrogen salt solution of hydrogen phosphate dissolved in water to obtain a magnesium phosphate cement with high water resistance without a retarder. The invention has the characteristics of high strength (28d compressive strength is not less than 100MPa), long setting time (initial setting time is not less than 30min), good water resistance (56d, strength retention rate can reach more than 95%).

【技术实现步骤摘要】
一种无需缓凝剂的高耐水性磷酸镁水泥
本专利技术属于磷酸镁水泥的制备领域，具体涉及一种无需缓凝剂的高耐水性磷酸镁水泥。
技术介绍
磷酸镁水泥（Magnesiumphosphatecement，MPC）作为一种新型的气硬性胶凝材料，同时兼具化学结合陶瓷的属性，具有一系列传统结构材料无以比拟的性能：凝结硬化迅速、早期强度高、粘结强度高、耐热性和耐磨性良好等优点，被大量应用于水泥混凝土的快速修补领域，如飞机跑道、公路和桥面等。磷酸盐是磷酸镁水泥的主要组分之一，主要为磷酸镁水泥反应提供酸性组分。目前，磷酸镁水泥常用磷酸盐主要有NH4H2PO4和KH2PO4及两者的复合。也有学者研究用磷酸一氢盐如(NH4)2HPO4、K2HPO4和电解镁砂制备磷酸镁水泥，指出虽然采用磷酸一氢盐较磷酸二氢盐相比，水泥的凝结时间变长，但强度比磷酸二氢盐要低很多，几乎没有强度。磷酸镁水泥其凝结硬化时间很短，几分钟内就凝结硬化，完全失去工作性能；增大水胶比可以提高其施工性能，但是强度下降很大；增加缓凝剂的掺量，虽然可以延长其凝结时间，有利于工作性能的保持，但同时使其强度下降，特别是小时强度下降很明显。并且磷酸镁水泥的强本文档来自技高网...

【技术保护点】
一种无需缓凝剂的高耐水性磷酸镁水泥，其特征在于：由烧结氧化镁、磷酸氢二盐、水和硅灰四种原料制成。

【技术特征摘要】
1.一种无需缓凝剂的高耐水性磷酸镁水泥，其特征在于：由烧结氧化镁、磷酸氢二盐、水和硅灰四种原料制成。2.根据权利要求1所述的无需缓凝剂的高耐水性磷酸镁水泥，其特征在于：按重量份数计，烧结氧化镁50～70份，磷酸氢二盐10～40份，硅灰10～20份；加水量为烧结氧化镁、硅灰和磷酸氢二盐重量之和的0.14-0.18倍扣除磷酸氢二盐溶于水所释放出的结晶水的量。3.根据权利要求1或2所述的无需缓凝剂的高耐水性磷酸镁水泥，其特征在于...

【专利技术属性】
技术研发人员：林旭健，潘晓鑫，季韬，辛东升，
申请(专利权)人：福州大学，
类型：发明
国别省市：福建,35