The invention discloses a photo album inner plate modified coating comprises the following components: the weight percentage of kaolin / calcium carbonate 100 copies, 35 copies, 25 adhesive dispersant 0.5 1.5, 0.1 resistance agent 0.3 and water 100 copies, 0.9 copies of the 0.2 stripping agent; wherein, the adhesive for benzene acrylic latex / SBR latex dispersant, sodium polyacrylate, stripping agent for oxidized polyethylene wax, water resistant agent for ammonium zirconium carbonate. After the invention is coated on the inner core board of the photo album, the inner core board of the album can be ensured to have a smooth surface and good visual effect, and can not deform after being placed for a long time, and the service life is long.
【技术实现步骤摘要】
相册内芯板修饰涂料及其制备方法
本专利技术涉及一种相册内芯板修饰涂料及其制备方法。
技术介绍
传统的相册内芯板通常采用涂布白板纸，然而这种内芯板易分层，只能勉强满足相册纸的要求，长时间放置易变形，不适合相册长时间保存，影响相册的使用寿命。为了提高相册的使用寿命，出现了一种不易分层变形的内芯板，但是该内芯板的表面凹凸不平，视觉效果差。
技术实现思路
本专利技术为了解决目前相册纸表面凹凸不平的问题，为此提供了一种相册内芯板修饰涂料及其制备方法。本专利技术的技术方案如下：一种相册内芯板修饰涂料，包括以下百分比重量的组份：其中，胶黏剂为苯丙胶乳/丁苯胶乳，分散剂为聚丙烯酸钠，剥离剂为氧化聚乙烯蜡，抗水剂为碳酸锆铵。苯丙胶乳/丁苯胶乳的固含量为48-50％。一种相册内芯板修饰涂料的制备方法，包括：(1)重量份数为0.5-1.5份的聚丙烯酸钠经100份水稀释后，加入100份高岭土/碳酸钙，并高速搅拌使分散均匀；(2)分散均匀后转为低速搅拌，并依次添加重量份数为25-35份的苯丙胶乳/丁苯胶乳、0.1-0.3份碳酸锆铵和0.2-0.9份氧化聚乙烯蜡，低速搅拌混合均匀制成相册内芯板修...
【技术保护点】
一种相册内芯板修饰涂料，其特征是在于，包括以下百分比重量的组份：高岭土/碳酸钙 100胶黏剂 25‑35分散剂 0.5‑1.5抗水剂 0.1‑0.3水 100剥离剂 0.2‑0.9其中，胶黏剂为苯丙胶乳/丁苯胶乳，分散剂为聚丙烯酸钠，剥离剂为氧化聚乙烯蜡，抗水剂为碳酸锆铵。
【技术特征摘要】
1.一种相册内芯板修饰涂料，其特征是在于，包括以下百分比重量的组份：高岭土/碳酸钙100胶黏剂25-35分散剂0.5-1.5抗水剂0.1-0.3水100剥离剂0.2-0.9其中，胶黏剂为苯丙胶乳/丁苯胶乳，分散剂为聚丙烯酸钠，剥离剂为氧化聚乙烯蜡，抗水剂为碳酸锆铵。2.根据权利要求1所述的相册内芯板修饰涂料，其特征是在于，苯丙胶乳/丁苯胶乳的固含量为48-50%。3.根据权利要求1所述的相册内芯板修饰涂料，其特征是在于，包括以下百分比重量的组份：高岭土/碳酸钙100苯丙胶乳/丁苯胶乳30聚丙烯酸钠1碳酸锆铵0.2水100氧化聚乙烯蜡0.9...
【专利技术属性】
技术研发人员：仰朝晖，
申请(专利权)人：江阴比图特种纸板有限公司，
类型：发明
国别省市：江苏,32