本发明专利技术属于耐火材料结合剂领域，涉及一种新型改性结合剂。葡萄糖作为结合剂在使用过程中残炭率较低，且热稳定性不高，所以通过一定的技术手段改善其使用特性。其技术方案是：将葡萄糖与催化剂按照一定比例混合，得到改性葡萄糖。本发明专利技术制备的改性结合剂经高温埋碳处理，会部分原位生成碳纳米管，不仅提高了结合剂的残炭率和抗氧化性能，而且成本低廉，环境友好。

Modified binding agent

The invention belongs to the field of refractory material bonding agent and relates to a novel modified binding agent. As the binding agent of glucose, the carbon residue rate is low and the thermal stability is not high, so it can be improved by some technical means. The technical proposal is that glucose is mixed with a catalyst in a certain proportion to obtain modified glucose. The modified binding agent prepared by the invention has the advantages of high temperature and carbon burial, and the carbon nanotubes can be formed partially in situ, thereby improving the carbon residue rate and the oxidation resistance of the binding agent, and having low cost and friendly environment.

【技术实现步骤摘要】
一种改性结合剂
本专利技术属于耐火材料结合剂领域，尤其涉及到一种改性结合剂。
技术介绍
在耐火材料中，有些原料之间润湿性较差，很难直接结合，这就需要结合剂的加入。传统耐火材料中，酚醛树脂以其结合能力强、制品强度大、碳化后残炭率高等优点被广泛用作结合剂。但是，酚醛树脂一方面价格较高，是产品成本提升；另一方面在固化、干燥的过程中会有刺激性气体氨气、甲醛等产生，污染环境而且在使用过程中环境温度影响较大，温度较低时，酚醛树脂粘度大，必须加热才能使用，生产上不方便。为了解决这些问题，专利技术专利CN101077523A探索得到一种新型结合剂-葡萄糖。相比于酚醛树脂，葡萄糖成本低廉，环境友好，在使用过程中不产生刺激性气体，而且，省去了树脂固化的过程，缩短了生产时间，提高了生产效率。但是，葡萄糖在使用过程中由于热分解温度较低，碳化后残炭率较低，使得制品强度较低，热稳定性差，因此对葡萄糖的改性研究具有现实意义。
技术实现思路
为了解决葡萄糖作为结合剂在使用过程中热分解温度低、残炭率低的问题，本专利技术在于提供一种残炭率高、热稳定性好且环保的改性结合剂。为了达到上述目的，本专利技术采用的技术方案是：取适量本文档来自技高网...

【技术保护点】
一种改性结合剂，其特征在于在葡萄糖中加入催化剂，混合均匀，得到改性结合剂，改性结合剂经碳化处理后，原位生成碳纳米管。

【技术特征摘要】
1.一种改性结合剂，其特征在于在葡萄糖中加入催化剂，混合均匀，得到改性结合剂，改性结合剂经碳化处理后，原位生成碳纳米管。2.权利要求1所述的改性结合剂，其特征在于催化剂的种类为过渡金属氧化物，如氧化钴、一氧化...

【专利技术属性】
技术研发人员：涂军波，李金雨，温军英，唐冰杰，连伟康，王义龙，陈永强，张连进，魏军从，
申请(专利权)人：华北理工大学，
类型：发明
国别省市：河北,13