一种固相法制备硫化锌‑银异质结纳米片的方法技术
A solid state synthesis of ZnS heterojunction silver nano sheet method
The invention relates to a solid preparation of ZnS heterojunction silver nano sheet method, which belongs to the field of nano material preparation. The method is twelve zinc acetate, sodium lauryl sulfate, thioacetamide, sodium borohydride and silver acetate at room temperature followed by mixing and grinding the solid state reaction, synthesis of ZnS heterojunction silver nano sheet. The prepared solid state chemical method of zinc sulfide silver heterojunction nano film has the characteristics of simple operation, without the use of solvent, high yield, low cost, simple synthesis process; and the prepared ZnS heterojunction Silver Nanoplates with large surface area and high reaction activity. Will have potential applications in optoelectronic devices, photocatalysis and other fields.
【技术实现步骤摘要】
一种固相法制备硫化锌-银异质结纳米片的方法
本专利技术涉及一种固相法制备硫化锌-银异质结纳米片的方法，属于纳米材料制备领域。
技术介绍
近年来，纳米材料由于其本身所具有的独特的物理化学特性而受到了科研工作者的广泛关注。二维纳米结构与纳米粉体不同，电子和光学激子在纳米结构中可有效传输，不仅具有小尺寸效应，表面效应，量子尺寸效应和宏观量子隧道效应等特殊性质，又存在由纳米结构组合引起的新的量子耦合效应和协同效应等，显示出优异的光学、电学性能，因而可以用作纳米器件及超大规模集成电路中的连接导线、光导纤维等。硫化锌-银异质结纳米片的制备及性能研究是当今纳米技术研究领域的一大焦点。目前，制备硫化锌-银异质结纳米片的方法众多，包括热蒸发法、物理气相沉积法（PVD）、水热法等。而这些方法涉及到实验条件苛刻、能耗高等不足，因而开发一种简单、高产、环境友好的合成方法仍然十分迫切。低热固相化学法具有操作简单、成本低、产量高和环境友好等优点，已经成为合成纳米材料的一种有效方法。
技术实现思路
本专利技术的目的在于提供一种硫化锌-银异质结纳米片的制备方法，是利用硼氢化钠的还原特性，采用低热固相化学反应来制备硫化锌-银异质结纳米片。该方法克服了硫化锌纳米材料在制备过程中发生严重团聚的现象，并实现了硫化锌与银的复合。本专利技术公开了一种固相制备硫化锌-银异质结纳米片的方法。本专利技术是将醋酸锌、十二烷基硫酸钠、硫代乙酰胺、硼氢化钠和醋酸银作为反应物，在室温下通过研磨发生反应，进而制得硫化锌-银异质结纳米片。本专利技术利用硼氢化钠的还原特性，运用固相合成工艺实现了硫化锌-银异质结纳米片的合成...
【技术保护点】
一种固相法制备硫化锌‑银异质结纳米片的方法，其特征是醋酸锌置于玛瑙研钵中，研细后加入十二烷基硫酸钠，研磨后加入硫代乙酰胺，研磨后加入硼氢化钠，研磨后加入适量醋酸银，再充分研磨并放置完成固相反应，用去离子水和无水乙醇洗涤，抽滤，在干燥箱中60度干燥2小时制得硫化锌‑银异质结纳米片。
【技术特征摘要】
1.一种固相法制备硫化锌-银异质结纳米片的方法，其特征是醋酸锌置于玛瑙研钵中，研细后加入十二烷基硫酸钠，研磨后加入硫代乙酰胺，研磨后加入硼氢化...