A nickel slag and silica fume concrete, including the following points: each weight aggregate 50 60 copies, 4 copies of 6 nickel slag, nickel slag sand 3 5 copies, 10 copies of the 6 natural sand, silica fume 3 5 copies, 20 copies of cement 15, water 5 8 a. The compressive strength of concrete is about 20MPa, the effective porosity and permeability coefficient of 15%~25% is about 3mm/s; good performance which is widely used in similar sidewalks, pedestrian street and parking lot and light load of roadbed and pavement engineering; concrete waste recycling, so that economic development and environmental protection to achieve the unity of. The goal of sustainable development; the invention saves natural resources, protect the ecological environment, has good economic effect and social effect.
【技术实现步骤摘要】
一种含镍渣与硅灰的混凝土
本专利技术涉及建筑材料
，特别是涉及一种含镍渣与硅灰的混凝土。
技术介绍
混凝土，简称为“砼（tóng）”：是指由胶凝材料将集料胶结成整体的工程复合材料的统称。通常讲的混凝土一词是指用水泥作胶凝材料，砂、石作集料；与水（可含外加剂和掺合料）按一定比例配合，经搅拌而得的水泥混凝土，也称普通混凝土，它广泛应用于土木工程。在北方寒冷地区和盐碱化地区，因环境恶劣，混凝土建筑物的冻害破坏，会产生裂缝和剥落等，另外盐碱化的侵蚀也均较严重，从而会导致混凝土工程的渗漏、开裂等，降低其耐久性和安全性。而普通混凝土得强度等级较低，抗冻性和抗侵蚀能力差，因而亟需一种抗冻和抗侵蚀能力强的混凝土。一方面，“水”是生命之源，是人类生存的根基，但如今水资源短缺以及水环境污染已经成为威胁人类发展的全球性问题。近年来，随着我国经济的快速发展，地下水严重过采，一些地区出现地陷的现象。同时，城镇化进程加快，越来越多的不透水硬质路面阻断了雨水回流，地下水得不到有效补给，加剧了水资源的危机，甚至导致气候反常，破坏了生态的平衡。另一方面，建筑废弃物的再生资源化利用能够使建筑业...
【技术保护点】
一种含镍渣与硅灰的混凝土，其特征是，所述含镍渣与硅灰的包括以下重量份的各组分：粗骨料50‑60份，镍渣粉 4‑6份，镍渣砂3‑5份，天然砂6‑10份，硅灰 3‑5份，水泥15‑20份，水5‑8份。
【技术特征摘要】
1.一种含镍渣与硅灰的混凝土，其特征是，所述含镍渣与硅灰的包括以下重量份的各组分：粗骨料50-60份，镍渣粉4-6份，镍渣砂3-5份，天然砂6-10份，硅灰3-5份，水泥15-20份，水5-8份。2.根据权利要求1所述的一种含镍渣与硅灰的混凝土，其特征是，所述混凝土包括以下重量份的各组分：粗骨料52-58份，镍渣粉4.3-5.7份，镍渣砂3.3-4.7份，天然砂6.5-9.5份，硅灰3.4-4.8份，水泥15.4-19.4份，水5.2-7.6份。3.根据权利要求1所述的一种含镍渣与硅灰的混凝土，其特征是，所述混凝土包括以下重量份的各组分：粗骨料52.8-56.4份，镍渣粉4.5-5.5份，镍渣砂3.5-4.5份...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。