The invention discloses a liquid crystal screen antifouling coating antibacterial effect, the main components include: fluorinated polyether silicone compound, silicon powder, nano titanium dioxide, catalyst, fluorescent powder, silicone, dispersing agent and solvent. The coating by the material science and reasonable use ratio method, has good anti pollution, high temperature resistance, wear resistance, impact resistance and adhesion; the main raw material of the fluorescent powder is two stilbene derivative, the fluorescent powder has the fluorescence ratio force induced discoloration, this phenomenon has a high contrast, fluorescence the color change of obvious characteristics, very suitable for the use of the touch screen.
【技术实现步骤摘要】
一种具有抗菌效果的液晶屏防污涂料及其使用方法
本专利技术涂料领域，具体涉及一种具有抗菌效果的液晶屏防污涂料及其使用方法。
技术介绍
随着电子工业的发展，特别是智能手机、大屏幕电视、只能平板电脑等推广和应用，各种触摸屏技术的推广之后，由于高频率的使用这些产品，产品的显示器表面很容易变脏、刮伤以及被一些化学溶剂腐蚀，因此提高这些产品的防水、防污、防化学试剂、提高耐磨性均十分必要，开发一种各方面综合性能优异的液晶屏保护材料十分必要，目前市场上的涂料无法满足其要求。
技术实现思路
本专利技术的目的在于提供一种具有抗菌效果的液晶屏防污涂料以及使用方法。一种具有抗菌效果的液晶屏防污涂料，由如下重量百分比的组分组成：氟化聚醚硅氧烷化合物30-50%硅微粉5-10%纳米二氧化钛0.2-0.5%催化剂0.5-1%荧光粉1-3%硅氧烷2-5%分散剂1-2%溶剂余量。优选的，氟化聚醚硅氧烷化合物的分子量为3000-5000。优选的，所述的催化剂为氧化锌；所述的荧光粉的主要原料为二苯乙烯衍生物，具有力致荧光比率变色现象，该现象具有对比度高，荧光颜色转变明显的特点，非常适合触摸屏使用。优选的，...
【技术保护点】
一种具有抗菌效果的液晶屏防污涂料，其特征在于，由如下重量百分比的组分组成：氟化聚醚硅氧烷化合物 30‑50%硅微粉 5‑10%纳米二氧化钛 0.2‑0.5%催化剂 0.5‑1%荧光粉 1‑3%硅氧烷 2‑5%分散剂 1‑2%溶剂 余量。
【技术特征摘要】
1.一种具有抗菌效果的液晶屏防污涂料，其特征在于，由如下重量百分比的组分组成：氟化聚醚硅氧烷化合物30-50%硅微粉5-10%纳米二氧化钛0.2-0.5%催化剂0.5-1%荧光粉1-3%硅氧烷2-5%分散剂1-2%溶剂余量。2.如权利要求1所述的具有抗菌效果的液晶屏防污涂料，其特征在于，氟化聚醚硅氧烷化合物的分子量为3000-5000。3.如权利要求1所述的具有抗菌效果的液晶屏防污涂料，其特征在于，所述的催化剂为氧化锌；所述的荧光粉的主要原料为二苯乙烯衍生物，具有致比率荧光变色现象。4.如权利要求1所述的具有抗菌效果的液晶屏防污涂料，其特征在于，所述的分散剂为润湿剂X-405。5.如权利要求1所述的具有抗菌效果的液晶屏防污涂料，其特征在于，所述的溶剂为有机溶剂...