The invention relates to a polylactic acid modified material with high strength, good heat resistance and controllable degradation, and a preparation method thereof, which is a polymer compound field. The modified material used as raw material of polylactic acid: 10 90 copies, 30 copies, 1 filler: crosslinking agent: 1 5, heat-resisting toughening agent: 1 10; 2: 0.2 assisted degradation agent; the invention of the modified polylactic acid material the use of more environmentally friendly raw materials, simple process, low cost, significantly improve the toughness and heat resistance of poly lactic acid and first introduced green photocatalyst nano TiO2 and calcium lactate, can selectively change the material degradation performance. It can promote the further industrialization and popularization of pla.
【技术实现步骤摘要】
一种强度高耐热性好且降解性可控的聚乳酸改性材料及其制备方法
本专利技术涉及一种强度高耐热性好且降解性可控的聚乳酸改性材料及其制备方法,属于高分子材料
技术介绍
聚乳酸（PLA），别名聚丙交酯，是一种重要的乳酸衍生物，是以乳酸为单体经化学合成或生物合成得到的一类高分子材料。聚乳酸具有无毒无刺激、优良的生物相容性、易降解、可塑性强、易加工成型等优点，在高分子材料行业备受青睐，而在环境保护方面更是具有广阔的应用前景。聚乳酸虽然具有优异的生物相容性及易降解性，对环境十分友好的特点，但聚乳酸仍有许多不足之处，如强度低，韧性差，热变形温度低等问题，限制了其进一步发展和广泛使用。故需要通过对聚乳酸改性研究来增强其性能，以拓宽其应用价值。纳米TiO2亦称钛白粉，为白色疏松粉末，屏蔽紫外线作用强，有良好的分散性和耐候性，在汽车工业及诸多领域都显示出美好的发展前景。纳米TiO2还具有很高的化学稳定性、热稳定性、无毒性、超亲水性、非迁移性，且完全可以与食品接触，所以被广泛用于诸多行业。针对聚乳酸耐热温度低，强度低的缺点，不少国内外对此做了很多工作，但很少有技术说到同时提高耐热...
【技术保护点】
一种强度高耐热性好且降解性可控的聚乳酸改性材料，其特征为：由下列质量份数的原料制成：聚乳酸：10‑90份、填充剂：1‑30份、交联剂：1‑5份、耐热增韧改性剂：1‑10份；辅助降解剂：0.2‑2份。
【技术特征摘要】
1.一种强度高耐热性好且降解性可控的聚乳酸改性材料，其特征为：由下列质量份数的原料制成：聚乳酸：10-90份、填充剂：1-30份、交联剂：1-5份、耐热增韧改性剂：1-10份；辅助降解剂：0.2-2份。2.如权利要求1所述的一种强度高耐热性好且降解性可控的聚乳酸改性材料，其特征为：聚乳酸为平均分子量在5万-15万的L-聚乳酸和D-聚乳酸中的一种或两种。3.如权利要求1所述的一种强度高耐热性好且降解性可控的聚乳酸改性材料，其特征为：填充剂为纳米碳酸钙和细度不小于5000目的蒙脱土中的一种或两种。4.如权利要求1所述的一种强度高耐热性好且降解性可控的聚乳酸改性材料，其特征为：交联剂为聚乙二醇和聚丙二醇中的一种或两种。5.如权利要求...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。