埃洛石负载针形四氧化三铁纳米复合材料的制备方法技术
Preparation method of galapectite loaded needle Fe3O4 nano composite material
Preparation method of galapectite loaded needle Fe3O4 nano composite material, which belongs to the technical field of water treatment. The mixture of natural mineral soil halloysite and iron salt solution after adding alkali solution, the reaction in an inert gas atmosphere, and then the reaction product obtained after magnetic separation of solid solid; then using deionized water and ethanol washing to neutral, after freeze drying to galapectite loaded needle Fe3O4 nano composite material. The prepared nano composite material overcomes the agglomerationof nanomaterials inactivation, two pollution water problems and the existing problems of removing arsenic, arsenic has good adsorption performance, the water arsenic had high removal efficiency, and can effectively remove trivalent arsenic, the preparation process is simple and reliable, the production cycle is short.
【技术实现步骤摘要】
埃洛石负载针形四氧化三铁纳米复合材料的制备方法
本专利技术属于水处理
，具体涉及水体砷净化材料的制备技术。
技术介绍
砷是普遍存在于自然界中的一种准金属元素，根据形态不同，砷可以分为无机砷和有机砷。根据化合价不同，砷又可分为正五价砷As（V）和正三价砷As（III）。其中正三价无机砷毒性最高。由于砷的剧毒性和迁移特性，砷污染对人类的健康和生态环境产生了巨大的威胁，水体砷污染已经引起世界范围内的广泛关注。美国环境保护署(USEPA)和世界卫生组织(WHO)以及中国现行标准都规定了，饮用水中砷的含量标准为10ppb。因此，如何有效、便捷的去除水体中的砷是关系到人类健康的重要课题。在众多砷污染的处理方法中，吸附法已经被证实为最简单有效、相对经济的处理方法，各类吸附材料被研究者开发出来，许多研究结果表明，铁氧体基和壳聚糖基吸附材料可以有效去除水体中高浓度的砷，因为他们对无机砷有很强的亲和力，然而此类材料也存在着一定的缺陷，如吸附不够彻底，吸附效率较慢、吸附容量低、成本较高、不能达到饮用水标准，且对毒性最高的三价无机砷去除效率低。纳米材料由于尺寸小、比表面积高、吸附能...
【技术保护点】
埃洛石负载针形四氧化三铁纳米复合材料的制备方法，其特征在于包括以下步骤：1）将天然矿土埃洛石与铁盐水溶液混合；2）在步骤1）所得的混合物中加入碱溶液，在惰性气体氛围中进行反应，然后将反应产物经磁分离取得固相物；3）将固相物以去离子水和乙醇洗涤至中性，经冷冻干燥，得埃洛石负载针形四氧化三铁纳米复合材料。
【技术特征摘要】
1.埃洛石负载针形四氧化三铁纳米复合材料的制备方法，其特征在于包括以下步骤：1）将天然矿土埃洛石与铁盐水溶液混合；2）在步骤1）所得的混合物中加入碱溶液，在惰性气体氛围中进行反应，然后将反应产物经磁分离取得固相物；3）将固相物以去离子水和乙醇洗涤至中性，经冷冻干燥，得埃洛石负载针形四氧化三铁纳米复合材料。2.根据权利要求1所述的制备方法，其特征在于：所述铁盐为硫酸铁、硝酸铁、氯化铁、草酸铁、硫酸亚铁、氯化亚铁或乙酸铁中的...
【专利技术属性】
技术研发人员：宋晓丽，周蕾，李凌，张树伟，
申请(专利权)人：扬州大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。