一种基于氧化石墨烯的疏水性吸附剂制造技术
Hydrophobic adsorbent based on graphene oxide
The present invention discloses a hydrophobic adsorbent based on graphene oxide. The invention relates to a hydrophobic adsorbent for three-dimensional oxidation of graphene with fluorine compounds, and Its Adsorption Application to methylene blue dye. The invention provides a method for modifying graphene oxide by using fluorine monomer, and there is no report about the modification of graphene oxide by fluorine containing monomer at present. The modified graphene oxide prepared by the invention has the advantages of fluffy and porous foams, large specific surface area, low density and stable structure, and the preparation process is simple and easy to control.
【技术实现步骤摘要】
一种基于氧化石墨烯的疏水性吸附剂
本专利技术涉及一种基于氧化石墨烯的疏水性吸附剂，具体为一种氧化石墨烯/含氟化合物复合材料(改性氧化石墨烯泡沫)的制备方法，属于无机化学
技术介绍
石墨烯是一种由碳原子构成的单层片状结构的新材料，是目前所发现的最薄的二维材料。目前，石墨烯的制备方法主要有：微机械剥离法、外延生长法、化学气相沉积(CVD)法、氧化石墨还原法及碳纳米转换法等。与二维晶体石墨烯相比，改性后的三维氧化石墨烯具有较二维石墨烯更高的比表面积和活性。具有比表面大、吸附能力强、机械强度高、易于制备等优良特性，这些独特的性质使得改性氧化石墨烯海绵吸附材料成为环境污染处理中的热点。染料是主要的水污染物质，来源于印刷、纺织、印染及造纸等行业。大部分的染料分子结构复杂稳定，难以生物降解。传统的吸附剂有活性炭、树脂、聚氨酯泡沫、矿物及其废弃物。活性炭再生困难，处理成本较高，因此应用面窄，一般仅用于浓度较低的染料废水处理；树脂吸附应用较少，成本高；聚氨酯泡沫一般用于重金属废水、水中浮油、水中苯酚等有机污染物吸附，对染料废水应用较少；矿物及其废弃物吸附易引入重金属离子，...
【技术保护点】
一种基于氧化石墨烯的疏水性吸附剂，其特征在于，所述吸附剂的制备方法如下：1)氧化石墨烯的制备方法：取原材料天然石墨，硝酸钠，高锰酸钾和浓硫酸分别在冰浴3℃‑8℃和油浴35℃‑98℃中搅拌完成氧化实验；2)分离提纯：将上述混合液通过离心机离心，之后用透析袋透析至溶液pH接近中性；3)改性氧化石墨烯的制备：向上述混合液中加入交联剂功能酰胺类单体和含氟单体，在50‑80℃油浴反应2‑8h；4)改性氧化石墨烯的冷冻干燥：将步骤3)的混合液超声30‑60分钟后，固定在模具里，放入冷冻干燥箱中进行冷冻干燥，制备出改性氧化石墨烯泡沫即本专利技术基于氧化石墨烯的疏水吸附剂。
【技术特征摘要】
1.一种基于氧化石墨烯的疏水性吸附剂，其特征在于，所述吸附剂的制备方法如下：1)氧化石墨烯的制备方法：取原材料天然石墨，硝酸钠，高锰酸钾和浓硫酸分别在冰浴3℃-8℃和油浴35℃-98℃中搅拌完成氧化实验；2)分离提纯：将上述混合液通过离心机离心，之后用透析袋透析至溶液pH接近中性；3)改性氧化石墨烯的制备：向上述混合液中加入交联剂功能酰胺类单体和含氟单体，在50-80℃油浴反应2-8h；4)改性氧化石墨烯的冷冻干燥：将步骤3)的混合液超声30-60分钟后，固定在模具里，放入冷冻干燥箱中进行冷冻干燥，制备出改性氧化石墨烯泡沫即本发明基于氧化石墨烯的疏水吸附剂。2.根据权利要求1所述的基于氧化石墨烯的疏...