The invention discloses a process for producing seamless stereo socks uppers, cotton, artificial cotton, wool spinning, chemical fiber, silk and other textile materials in one or more as basic material, coupled with thermal fuse, woven into the double double socks; socks in the shoe last in the oven the heating temperature of hot flashes, is 80 to 150 DEG C; heating time is 1 ~ 5min; remove the socks from the oven, for natural cooling or cooling, the socks from last out, after setting a vamp socks socks; socks uppers and soles and at the same time can be bonded together to form the socks, shoes, socks made the traditional shoes shoes have stereo feeling, easy to wear, safe and reliable.
【技术实现步骤摘要】
一种立体无缝袜子鞋面、袜鞋的生产工艺
本专利技术涉及制袜和制鞋领域，更具体地说，它涉及一种立体无缝袜子鞋面、袜鞋的生产工艺。
技术介绍
鞋子是人们必不可少的生活用品。鞋子一般由两个部分组成，鞋面和鞋底。鞋面的材料一般为天然真皮、人造革(PUPVC)、布料(帆布、超纤布、尼龙布等其他布料)。近年来随着横机织造的飞织鞋面的技术进步和产品的普及，在鞋面的生产和制造方面上，生产效率得到了很大的提高而且极大地节约了材料，在这种背景之下，人们开始思考是否有一种新的制造方法和制造工艺比飞织的生产方法更能提高制造鞋面的效率并且更加节约材料。通常穿着鞋子时，都需要穿着袜子，传统的袜子穿着在脚上才有脚的形状，但传统的袜子本身不能形成脚一样的立体形状的。如果把传统的袜子和鞋底粘合在一起形成的一种以袜子为鞋面的鞋子，我们称之为袜鞋，存在以下缺陷：1、袜鞋软塌塌的，没有常见的鞋子的那种立体感；2、袜子有弹力具有伸缩性，袜鞋穿在脚上，脚一移动一着地，脚就会左右滑动，或前冲后仰，没有着地感，没有支撑，脚站不稳，容易跌倒。
技术实现思路
针对现有技术存在的不足，本专利技术的目的在于提供一种立体无缝袜...
【技术保护点】
一种立体无缝袜子鞋面的生产工艺，其特征是：包括如下步骤：(1)、由棉纱、人造棉、毛纺纱、化纤、真丝等纺织材料中的一种或一种以上为基础原料，再加上热熔丝，编织成双层袜子；(2)、将该双层袜子套在鞋楦上，放入烘箱内进行烘热，其中烘热的温度为：80～150℃；烘热时间为1～5min；将袜子从烘箱取出，进行自然降温或者冷却后，把袜子从鞋楦取出，袜子经过定型后成为袜子鞋面；(3)、将该袜子鞋面，经检品合格后包装入库。
【技术特征摘要】
1.一种立体无缝袜子鞋面的生产工艺，其特征是：包括如下步骤：(1)、由棉纱、人造棉、毛纺纱、化纤、真丝等纺织材料中的一种或一种以上为基础原料，再加上热熔丝，编织成双层袜子；(2)、将该双层袜子套在鞋楦上，放入烘箱内进行烘热，其中烘热的温度为：80～150℃；烘热时间为1～5min；将袜子从烘箱取出，进行自然降温或者冷却后，把袜子从鞋楦取出，袜子经过定型后成为袜子鞋面；(3)、将该袜子鞋面，经检品合格后包装入库。2.根据权利要求1所述的一种立体无缝袜子鞋面的生产工艺，其特征是：步骤(1)中的双层袜子编织包括如下步骤：1)、选择袜机将添加有热熔丝的基础原料编织成里层...