The invention discloses a supported Pd catalyst and preparation method and application thereof, which is Pd of LaFeO3 semiconductor nanoparticles carrier to absorb light in has, prepared the Pd catalyst, whereby the catalytic converter with load type catalyst Pd in the introduction of flexible LED strip lights, to achieve efficient catalysis CO/NO by photothermal coupling removal. Compared with the conventional thermal catalytic reaction, the thermal coupling method can greatly reduce the temperature of the catalyst, and the flexible LED lamp with lamp more than conventional anti vibration, is conducive to the removal of NO and CO are widely used in automotive exhaust purification.
【技术实现步骤摘要】
一种负载型Pd催化剂及其制备方法和应用
本专利技术属于环境保护及空气净化领域，具体涉及一种负载型Pd催化剂及其制备方法与应用，该负载型Pd催化剂可通过光热耦合作用提高对CO和NO的催化去除效果。
技术介绍
随着城市汽车的迅速增加，汽车尾气排放已经成为城市主要的空气污染源之一。汽车尾气的排放不仅给我们的生活、环境造成了极大的危害，同时对人体的健康也是一种不可忽视的伤害。大气自我净化能力已不足以降解汽车尾气，所以，解决汽车尾气污染，还人类一个洁净的环境已迫在眉睫。科学分析表明，汽车尾气中含有上百种不同的化合物，其中的污染物有固体悬浮微粒、一氧化碳、二氧化碳、碳氢化合物、氮氧化合物、铅及硫氧化合物等。对于汽车尾气排放量的控制，在各国的政策上经历了一系列的变革，从最初的仅限制CO的排放，到限制CO和HCs的排放，到最后一体化的限制CO、HCs和氮氧化物NO的排放；同时，在科学研究上，人们一直尝试从化学燃料、发动机燃烧效率、催化剂等各方面来控制汽车尾气中对大气污染较严重的气体，尤其是一氧化碳CO，碳氢化合物HCs和氮氧化物NOx。治理汽车排气污染的技术手段主要可分为三类:一...
【技术保护点】
一种负载型Pd催化剂，其特征在于：所述催化剂是以LaFeO3为载体，Pd纳米粒子为活性组分构成的高分散负载型催化剂；其中，活性组分Pd的含量为0.5‑2.5wt%；所述负载型Pd催化剂在可见光照条件下，能够在60‑120℃的低温下实现汽车尾气中CO及NO的去除。
【技术特征摘要】
1.一种负载型Pd催化剂，其特征在于：所述催化剂是以LaFeO3为载体，Pd纳米粒子为活性组分构成的高分散负载型催化剂；其中，活性组分Pd的含量为0.5-2.5wt%；所述负载型Pd催化剂在可见光照条件下，能够在60-120℃的低温下实现汽车尾气中CO及NO的去除。2.一种制备如权利要求1所述的负载型Pd催化剂的方法，其特征在于：先利用表面活性剂PVP为软模板剂辅助合成LaFeO3载体；再利用沉积沉淀法在所得LaFeO3载体上负载活性组分Pd。3.根据权利要求2所述的负载型Pd催化剂的制备方法，其特征在于：包括以下步骤：（1）在PVP的醇溶液中加入等摩尔比的Fe(NO3)3·9H2O和La(NO3)3·6H2O作为前驱体，搅拌、干燥、煅烧制得LaFeO3载体；（2）在所得LaFeO3载体中加入PdCl2溶液及去离子水，搅拌30-60min，超声15-30min，随后加入过量...
【专利技术属性】
技术研发人员：戴文新，程刚，陈旬，付贤智，员汝胜，丁正新，