一种低碳含碳耐火材料用酚醛树脂基微纳米石墨薄片混合料的制备方法技术
Method for preparing phenolic resin based micro nano graphite sheet mixture for low-carbon carbon containing refractory material
The present invention relates to a phenolic resin with a low carbon carbon containing refractory micro nano graphite sheet mixture preparation method, the technical scheme is: first 0.1~15wt% graphite (graphite) materials into pre mixed 85~99.9wt% phenolic resin, then the mixture from the feed roller to three roller grinding machine for roll three differential cyclic stripping, three roll rate is 1:3:9, the gap between the three rollers is 0.1~30 m, 2 Cyclic stripping after 50 times, micro nano graphite / from the discharge and collected the prepared phenolic resin mixture. The graphite nanosheets / prepared phenolic resin mixture is mainly used for preparing carbon containing refractories, can maintain / achieve carbon content increased with the comprehensive performance of carbon refractories based on greatly reduced.
【技术实现步骤摘要】
一种低碳含碳耐火材料用酚醛树脂基微纳米石墨薄片混合料的制备方法
本专利技术涉及一种低碳含碳耐火材料用酚醛树脂基微纳米石墨薄片混合料及其制备方法，属于耐火材料
技术介绍
碳素材料具有良好的耐高温性、化学稳定性和抗热震稳定性，特别是与熔融金属铁液的界面张力大而不被润湿等特点，被广泛应用于钢铁冶炼工业用含碳耐火材料中，能够显著提高其抗渣侵蚀和抗热震性能。现有国内外大型钢厂用含碳耐火材料的碳素原料使用最多的是天然鳞片石墨，传统含碳耐火材料由于含有较高的碳含量（一般10-20wt%的碳含量）导致抗氧化性差、机械强度低等严重问题。其次，高碳含量引起的高热导率会导致巨大热损失的产生、钢水的降温、炼钢炉钢壳体的形变，造成能源的浪费和钢铁铸造过程的扰乱；第三，含碳耐火材料中与钢水直接接触的碳在钢水中会发生溶解，耐火材料的脱碳会造成钢水中碳含量的增加改变钢的组成使得当前含碳耐火材料（砖）不适于制作高档洁净钢和超低碳钢的内衬材料；第四，近些年石墨作为我国战略性资源，随着开采越来越严格，大量石墨被消耗在高含碳耐火材料中造成石墨资源的浪费；第五，要避免这些大量的石墨/碳的氧化，需...
【技术保护点】
一种低碳含碳耐火材料用酚醛树脂基微纳米石墨薄片混合料的制备方法，其特征在于：（1）先将0.1~15wt%碳质原料倒入85~99.9wt%酚醛树脂中进行预混合；（2）再将混合物从进料辊加入三辊研磨机进行三辊差速循环剥离，循环剥离2‑50次后，从出料辊收集得到该专利技术所制备的酚醛树脂基微纳米石墨薄片混合料。
【技术特征摘要】
1.一种低碳含碳耐火材料用酚醛树脂基微纳米石墨薄片混合料的制备方法，其特征在于：（1）先将0.1~15wt%碳质原料倒入85~99.9wt%酚醛树脂中进行预混合；（2）再将混合物从进料辊加入三辊研磨机进行三辊差速循环剥离，循环剥离2-50次后，从出料辊收集得到该发明所制备的酚醛树脂基微纳米石墨薄片混合料。2.根据权利要求1所述的一种低碳含碳耐火材料用酚醛树脂基微纳米石墨薄片混合料的制备方法，其特征在于：所述的碳质原...