The invention discloses a method for preparing composite additives, and graphite materials in a new production of low resistance graphite material wherein the mixture of the compound additive of rare earth metal powder or rare earth compounds and nickel metal powder or nickel compounds, two kinds of material mixed when the mass ratio of 1:1 to 1:5; one or several of the rare earth rare earth rare earth compound selected from the group consisting of organic compounds and inorganic compounds; one or several of the nickel nickel nickel compound selected from the group consisting of organic compounds and inorganic compounds.
【技术实现步骤摘要】
一种新型生产低电阻石墨材料的复合添加剂及该石墨材料的制备方法
本专利技术涉及石墨材料
，具体地说，涉及一种新型生产低电阻石墨材料的复合添加剂及该低电阻石墨材料的制备方法。
技术介绍
石墨化过程中影响石墨产品性能的关键因素之一是气胀，焙烧品在石墨化炉中，当温度升高到1400℃以上时，氢、硫、氮等元素将以H2、H2S、N2、NH3等形式释放出来，其中氮元素主要在1400～1900℃释放出来，而硫元素集中在1700～2100℃区间释放出来，此时处于可塑状态的焦炭气孔壁受到排除气体的压力，体积产生膨胀，降低了石墨产品的物化性能。而通过添加气胀抑制剂或控制石墨化过程中1700～2100℃这一温度区间的升温速率，均能降低这一区间杂质气体的释放速率，从而有效的抑制气胀。催化石墨化可在满足性能要求的前提下，降低石墨化温度(石墨化度不降低)，简化对设备的要求，减少热应力，缩短石墨化时间，实现节能降耗，降低生产制造成本。例如，在制备过程中，通过添加氧化铁，可有效降低石墨化温度并抑制气胀，添加氧化铁的方案已经在工程领域中加以应用。然而铁又是对石墨制品有害的元素，过多的加入将影响石...
【技术保护点】
一种新型生产低电阻石墨材料的复合添加剂，其特征在于，该复合添加剂为稀土金属粉末或稀土化合物与镍金属粉末或镍化合物的混合物，两种物质混合时的质量比为1:1～1:5；所述稀土化合物选自稀土有机化合物和稀土无机化合物中的一种或几种；所述镍化合物选自镍有机化合物和镍无机化合物中的一种或几种。
【技术特征摘要】
1.一种新型生产低电阻石墨材料的复合添加剂，其特征在于，该复合添加剂为稀土金属粉末或稀土化合物与镍金属粉末或镍化合物的混合物，两种物质混合时的质量比为1:1～1:5；所述稀土化合物选自稀土有机化合物和稀土无机化合物中的一种或几种；所述镍化合物选自镍有机化合物和镍无机化合物中的一种或几种。2.根据权利要求1所述一种新型生产低电阻石墨材料的复合添加剂，其特征在于，所述稀土金属粉末或稀土化合物与镍金属粉末或镍化合物混合时，两种物质的质量比为1:3。3.根据权利要求1所述一种新型生产低电阻石墨材料的复合添加剂，其特征在于，所述稀土化合物为稀土氧化物、稀土碳化物和稀土卤化物中的一种或几种；所述镍化合物为氧化镍和/或碳化镍。4.根据权利要求1所述一种新型生产低电阻石墨材料的复合添加剂，其特征在于，所述稀土化合物为RE2O3、RE6O11和REX3中的一种或几种，所述RE为稀土元素，所述REX3中的X为Cl、Br或I；所述镍化合物为Ni2O3、NiC和NiY4中的一种或几种，所述NiY4中的Y为Cl、...
【专利技术属性】
技术研发人员：路贵民，王榕艳，于建国，
申请(专利权)人：华东理工大学，
类型：发明
国别省市：上海,31