The invention relates to a concrete water release agent and its preparation method and use method, raw materials concrete water release agent according to the weight, including: N N-isopropylacrylamide 5 ~ 10 weight, N, N 'methylenebisacrylamide 0.25 to 0.5 parts by weight of water and 85 to 95 parts by weight; the preparation method comprises the following steps: all the raw materials were mixed evenly, then ultrasonic vibration has been expanded; expansion will soak in the water after drying to constant weight; the product after drying, crushing, sieving and set, water release agent of concrete. The concrete moisture releasing agent provided by the invention can effectively improve the hydration of cement in concrete, improve the strength and reduce the shrinkage property of concrete.
【技术实现步骤摘要】
混凝土水分缓释剂及其制备方法与使用方法
本专利技术涉及建筑材料
，具体涉及一种混凝土水分缓释剂及其制备方法与使用方法。
技术介绍
随着我国经济和社会的发展，对于各类建筑、桥梁、地下建筑物等的要求越来越高，其中混凝土的强度和耐久性方面尤为重视。目前主要是通过掺入活性掺合料和高效减水剂来提高混凝土强度。但加入高效减水剂，会使混凝土用水量降低，水化不充分，增大混凝土的收缩，因此在混凝土实际施工中，如何在使用减水剂的情况下，提高水泥水化程度，降低混凝土收缩成了急需解决的问题。传统的混凝土养护方法有自然养护、常压蒸汽养护和高温高压养护等。正常情况下，人们都使用洒水或覆盖湿草包等自然养护方法。但传统的养护方法混凝土水化程度不高，难以发挥混凝土的最优状态。目前解决以上问题的方式是使用内养护。内养护是指在绝湿、绝热条件下依靠预吸水材料释放水分维持混凝土内部充分湿润的方法。国内主要的内养护剂分为三类：一是多孔结构的轻集料或陶粒，其吸水能力较低；二是纯高吸水性树脂，其分散性较差，释放不稳定；三是以植物淀粉等为原料合成，其制作工艺复杂且成本较高。因此研究一种能够克服以上问题并具有...
【技术保护点】
一种混凝土水分缓释剂，其特征在于，原料组分按重量份计，包括：N‑异丙基丙烯酰胺5～10重量份、N,N’‑亚甲基双丙烯酰胺0.25～0.5重量份和水85～95重量份。
【技术特征摘要】
1.一种混凝土水分缓释剂，其特征在于，原料组分按重量份计，包括：N-异丙基丙烯酰胺5～10重量份、N,N’-亚甲基双丙烯酰胺0.25～0.5重量份和水85～95重量份。2.根据权利要求1所述的混凝土水分缓释剂，其特征在于，所述原料组分还包括：过硫酸钾0.1～0.3重量份和亚硫酸氢钠0.1～0.3重量份。3.根据权利要求1或2所述的混凝土水分缓释剂，其特征在于：所述水为去离子水。4.权利要求1-3任一项所述的混凝土水分缓释剂的制备方法，其特征在于，包括如下步骤：S101：将所有原料组分混合均匀，然后进行超声波振动，得到膨胀物；S102：将所述膨胀物在水中浸泡；S103：将所述S102得到的产物干燥至恒重；S104：将所述干燥后的产物粉碎，再用套筛筛分，得到所述混凝土水分缓释剂。5.根据权利要求4所述的混凝土水分缓释剂的制备方法，其特征在于：所述S101中，所述超声波振动的温度为15～25℃，所述超声波振动的时间为20～40min，所述超声波振动的频率20～130kHz。6.根据权利要求4所述的混凝土水分缓释剂的...
【专利技术属性】
技术研发人员：郑娇玲，周铁柱，黄庆，佟莉，王若臣，王爱军，
申请(专利权)人：江苏超力建材科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。