A method of solid-phase preparation of zinc sulfide activated carbon composites
The invention relates to a method for preparing solid phase zinc sulfide activated carbon composite materials, which belongs to the field of nano material preparation. The method is twelve zinc acetate, sodium lauryl sulfate, thioacetamide and activated carbon at room temperature followed by mixing and grinding reaction, the low temperature synthesis of zinc sulfide activated carbon composites. Solid state chemical method for preparing zinc sulfide activated carbon composite material has the characteristics of simple operation, without the use of solvent, high yield, low cost, simple synthesis technology; and the preparation of zinc sulfide activated carbon composite material prepared with high surface area and high reaction activity, will have potential applications in optoelectronic devices, photocatalysis and other fields.
【技术实现步骤摘要】
一种固相制备硫化锌-活性炭复合材料的方法
本专利技术涉及一种固相法制备硫化锌-活性炭复合材料的方法，属于纳米材料制备领域。
技术介绍
近年来，纳米材料由于其本身所具有的独特的物理化学特性而受到了科研工作者的广泛关注。硫化锌作为一种十分重要的半导体纳米材料，因其具有特异的光、电、热、磁等性质，而在半导体发光器件、非线性光学材料、光催化等领域表现出巨大的应用前景。然而，ZnS半导体材料的禁带较宽，对可见光吸收弱成为制约其实际应用的重要因素。因而，对ZnS光催化剂进行改性研究是非常重要的研究领域。研究发现，活性炭因具有比表面积大、吸附性强等特性，而得到研究者的青睐，为此将硫化锌与活性炭复合可有效地改善其性能。硫化锌-活性炭复合材料的制备及性能研究是当今纳米技术研究领域的一大焦点。目前，制备硫化锌-银异质结纳米片的方法众多，包括热蒸发法、物理气相沉积法（PVD）、水热法等。而这些方法涉及到实验条件苛刻、能耗高等不足，因而开发一种简单、高产、环境友好的合成方法仍然十分迫切。低热固相化学法具有操作简单、成本低、产量高和环境友好等优点，已经成为合成纳米材料的一种有效方法。
技术实现思路
本专利技术的目的在于提供一种硫化锌-活性炭复合材料的制备方法，是利用活性炭比表面积大等特性，采用低热固相化学反应来制备硫化锌-活性炭复合材料。该方法克服了硫化锌纳米材料在制备过程中发生严重团聚的现象，并实现了硫化锌与活性炭的复合。本专利技术公开了一种固相制备硫化锌-活性炭复合材料的方法。本专利技术是将醋酸锌、十二烷基硫酸钠、硫代乙酰胺和活性炭作为反应物，在室温下通过研磨发生反应，进而制得硫化...
【技术保护点】
一种固相法制备硫化锌‑活性炭复合材料的方法，其特征是金属锌盐置于玛瑙研钵中，研细后加入十二烷基硫酸钠，研磨后加入硫代乙酰胺，研磨后加入适量活性炭，再充分研磨并放置完成固相反应，用去离子水和无水乙醇洗涤，抽滤，在干燥箱中60度干燥2小时制得硫化锌‑活性炭复合材料。
【技术特征摘要】
1.一种固相法制备硫化锌-活性炭复合材料的方法，其特征是金属锌盐置于玛瑙研钵中，研细后加入十二烷基硫酸钠，研磨后加入硫代乙酰胺，研磨...