The invention provides a two piece cans with steel plate and manufacturing method thereof, wherein the two cans of steel can not only reduce Bola with deep drawing processing, deep processing, and can deal with the edge, forming on the geometry of the tank body, can be preferably used for forming two sheet shaped tank. The above two cans of steel quality% above contains C:0.020% above and below 0.080%, Si:0.04%, Mn:0.10% and below 0.60%, below P:0.02%, below S:0.015%, Al:0.010% and N:0.0005%, the following 0.100% above and 0.0030% below, the remainder comprising Fe and inevitable impurities, wherein two cans with tensile strength for steel plate above 480MPa, the elongation is above 7%, the yield elongation is below 3%, the ferrite grain size less than 6 m.
【技术实现步骤摘要】
【国外来华专利技术】两片罐用钢板及其制造方法
本专利技术涉及适合于食品、饮料罐所使用的罐容器用材料的罐用钢板及其制造方法。本专利技术特别涉及成型性优异的两片罐用高强度钢板及其制造方法，本专利技术的两片罐用高强度钢板可以优选应用于在罐身部实施加工的两片异形罐。
技术介绍
从近年来降低环境负担及削减成本的观点考虑，要求降低用于食品罐、饮料罐的钢板的使用量。因此，无论是两片罐、三片罐，均在对作为原材料的钢板进行薄壁化。最近，为了补偿钢板的薄壁化所导致的罐体强度降低，大多制成对罐身部实施了卷边加工、赋予了几何形状的异形罐。在制造两片罐的异形罐(有时称为两片异形罐)的情况下，通过深冲加工、减薄拉深加工进行加工度较高的成型，然后对罐身部进行加工。因此，两片罐的异形罐的制造所使用的钢板要求更高的成型性。另一方面，加工度低的罐底部因加工硬化而带来的强度增加小。因此，在使钢板薄壁化的情况下，罐底部存在钢板的强度不足的倾向。特别是在罐底部的形状平坦的负压罐的情况下，需要现有的SR(SingleReduce)钢板以上的强度。因此，在罐底部使用即使薄壁化也易于进行高强度化的DR(DoubleReduce)钢...
【技术保护点】
一种两片罐用钢板，其以质量％计含有C：0.020％以上且0.080％以下、Si：0.04％以下、Mn：0.10％以上且0.60％以下、P：0.02％以下、S：0.015％以下、Al：0.010％以上且0.100％以下、N：0.0005％以上且0.0030％以下，余量由Fe及不可避免的杂质构成，所述两片罐用钢板的拉伸强度为480MPa以上，伸长率为7％以上，屈服伸长率为3％以下，铁素体粒径小于6μm。
【技术特征摘要】
【国外来华专利技术】2014.10.28 JP 2014-2189671.一种两片罐用钢板，其以质量％计含有C：0.020％以上且0.080％以下、Si：0.04％以下、Mn：0.10％以上且0.60％以下、P：0.02％以下、S：0.015％以下、Al：0.010％以上且0.100％以下、N：0.0005％以上且0.0030％以下，余量由Fe及不可避免的杂质构成，所述两片罐用钢板的拉伸强度为480MPa以上，伸长率为7％以上，屈服伸长率为3％以下，铁素体粒径小于6μm。2.根据权利要求1所述的两片罐用钢板，其中，以质量％计还含有B：0.0001％以上且0.0030％...
【专利技术属性】
技术研发人员：斋藤勇人，小岛克己，中丸裕树，
申请(专利权)人：杰富意钢铁株式会社，
类型：发明
国别省市：日本,JP