The invention discloses a metal bonded diamond grinding wheel, which is characterized by comprising a metal powder, copper cerium alloy, pore forming agent, TS 1 titanium silicon molecular sieve, composite diamond abrasive composition; the metal powder, iron powder, copper powder, nickel powder, tin powder; the pore forming agent is PE/CeO2/ Cu complex; the composite diamond abrasive diamond / ceria core-shell composite particles. The invention overcomes the defects of metal bonded diamond wheel self sharpening performance, low efficiency, metal bonded diamond grinding wheel of the invention has good mechanical properties and self sharpening, to diamond with high strength, good formability, long service life.
【技术实现步骤摘要】
一种金属结合剂金刚石砂轮
本专利技术属超硬材料制造领域，具体涉及一种金属结合剂金刚石砂轮。
技术介绍
金属结合剂是以合金粉或金属粉末为粘结材料,采用粉末冶金的工艺流程,通常用于超硬材料磨具制品的一种结合剂。金属结合剂具有较高的强度和较高的韧性，对磨粒的把持力较大，所以金属结合剂的超硬磨具具有使用寿命长、能承受较大的磨削压力等特点。其在工程陶瓷、石材加工、光学玻璃、硬质合金和电子元件等难加工材料的磨削加工中已得到了广泛应用。然而金属结合剂磨具存在自锐性差，磨具表面容易被堵塞等缺点。因此，在磨削加工中会出现工件表面容易被烧伤，工件的表面质量受到影响等问题。这在一定程度上使得金属结合剂磨具在一些精密加工的应用上受到了限制。为了解决金属结合剂磨具在高精度的精密加工中所存在的不足，国内外许多学者在结合剂改性上进行了大量的试验研究。其中，在金属结合剂配方中加入稀土元素来对金属结合剂进行改性受到了许多专家学者的关注。为了进一步提高和改善铁基金属结合剂的性能，采用添加Cu-Ce合金的方法，可以大大改善铁基金属结合剂性能的影响。
技术实现思路
本专利技术的目的正是针对上述现有技术中所存...
【技术保护点】
一种金属结合剂金刚石砂轮，其特征在于：该金属结合剂金刚石砂轮原料由铁粉、铜粉、锡粉、镍粉、铜铈合金、造孔剂、TS‑1钛硅分子筛、金刚石复合磨粒组成，各原料的重量百分比为：铁粉30%～50%、铜粉30%～50%、锡粉5%～10%、镍粉1%～2%、铜铈合金1%～10%、造孔剂1%～5%、TS‑1钛硅分子筛1%～5%、金刚石复合磨粒5%～15%；所述造孔剂为PE/CeO2/Cu复合物；所述金刚石复合磨粒为金刚石/氧化铈核壳复合磨粒。
【技术特征摘要】
1.一种金属结合剂金刚石砂轮，其特征在于：该金属结合剂金刚石砂轮原料由铁粉、铜粉、锡粉、镍粉、铜铈合金、造孔剂、TS-1钛硅分子筛、金刚石复合磨粒组成，各原料的重量百分比为：铁粉30%～50%、铜粉30%～50%、锡粉5%～10%、镍粉1%～2%、铜铈合金1%～10%、造孔剂1%～5%、TS-1钛硅分子筛1%～5%、金刚石复合磨粒5%～15%；所述造孔剂为PE/CeO2/Cu复合物；所述金刚石复合磨粒为金刚石/氧化铈核壳复合磨粒。2.根据权利要求1所述的金属结合剂金刚石砂轮，其特征在于：所述造孔剂是由挤出成型造粒得到的。3.根据权利要求1所述的金属结合剂金刚石砂轮，其特征在于：所述TS-1钛硅分子筛是经如下方法处理得到的：将200-300nm的TS-1钛硅分子筛浸入到5%-10%的硝酸铈的丙酮溶液中浸泡2-5h，经过滤，缓慢升温干...
【专利技术属性】
技术研发人员：陈金身，陈锋，智红梅，裴占柱，樊雪琴，董德胜，张朝阳，杜晓冉，王林圣，高正，
申请(专利权)人：河南工业大学，
类型：发明
国别省市：河南,41