The invention discloses a special defoaming agent for candles and candles. According to the weight percentage, the defoaming agent of raw materials including organosilicon compounds 10 ~ 80%, 2 ~ 50% octanol 5, sulfonated oil 5 ~ 50%, 5 ~ 50% organic phosphate, and triglycerides from 5 to 50%. The invention provides a candle, wax melting by adding the basis of defoaming agent and cooling molded, the basis for the paraffin wax, wax plant wax, animal fat based wax, wax mixed or any mixture of two or more. The defoaming agent can effectively reduce the surface tension of liquid wax, eliminate or reduce the bubbles in the liquid wax, good defoaming and antifoaming effect, can prevent the surface of the drum candle under high temperature bubble, can enhance the permeability of aroma. Moreover, the defoaming agent has very little use, and does not affect the overall appearance, performance and combustion performance of the candle.
【技术实现步骤摘要】
一种蜡烛专用消泡剂及蜡烛
本专利技术涉及蜡烛生产领域，特别是一种蜡烛专用消泡剂及添加了该消泡剂的蜡烛。
技术介绍
通常蜡烛在制作过程中，会加入一些添加剂，例如植物蜡、合成蜡、微晶蜡等，在多种类的添加剂中，有些与空气的结合力较强，结合了大量空气，在原料蜡混合时会不断释放出空气，导致最终产品产生气泡。另外，熔融蜡液一般具有很大的张力，同时在搅拌等工艺操作的影响下，凝固的蜡烛体内就会形成和隐藏较多的气泡和大气泡，这些气泡潜伏着很大风险，会造成蜡烛在高温环境下出现表面鼓泡现象，严重影响蜡烛的外观。同时这些气泡会包裹大量香精，在张力束缚作用下导致香精分子较难逃逸出来，蜡烛的香味透发性变差。因此，降低蜡液张力，消除或大量减少蜡液内的气泡是当务之急。消泡有多种方法，包括物理方法和化学方法，目前各行业中应用最广泛的是化学消泡法，具有破泡效率高、操作方便的优点。使用此方法的关键是选择合适的消泡剂，对于蜡液来说，同样如此。消泡剂添加在蜡烛原料体系中，一般通过使气泡液膜局部表面张力降低、破坏膜弹性失去自修功能、降低液膜粘度使气泡寿命缩短等机理来达到消泡的目的。单一化合物的消泡剂因其自身...
【技术保护点】
一种蜡烛专用消泡剂，其特征在于，按重量百分比计，原料包括有机硅化合物10～80％，2‑辛醇5～50％，磺化油5～50％，有机磷酸盐5～50％，以及油酸甘油酯5～50％。
【技术特征摘要】
1.一种蜡烛专用消泡剂，其特征在于，按重量百分比计，原料包括有机硅化合物10～80％，2-辛醇5～50％，磺化油5～50％，有机磷酸盐5～50％，以及油酸甘油酯5～50％。2.根据权利要求1所述的蜡烛专用消泡剂，其特征在于，所述有机硅化合物为聚二甲基硅氧烷。3.根据权利要求1所述的蜡烛专用消泡剂，其特征在于，所述油酸甘油酯为大豆甘油酯。4.根据权利要求1所述的蜡烛专用消泡剂，其特征在于，所述有机磷酸盐为磷酸三丁酯。5.根据权利要求1所述的蜡烛专用消泡剂，其特征在于，有机硅化合物为聚二甲基硅氧烷，用量为20...
【专利技术属性】
技术研发人员：刘小青，储新宏，姜颖，魏晓星，莫欣欣，
申请(专利权)人：青岛金王应用化学股份有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。