The invention relates to a preparation method of environmental protection and corrosion resistant cutting liquid, belonging to the technical field of cutting fluid preparation. The soybean dregs natural fermentation, through microbial decomposition of large proteins into amino acids, then the fermentation broth was concentrated after the formation of concentrated liquid, the rapeseed crushing and defatted with petroleum ether, acetone and concentrated liquid mixed extraction, extraction and collection of mixed surface active agent, defoaming agent mixture additives can be prepared a kind of environmental protection type corrosion resistant cutting fluid, cutting fluid prepared by the invention has good cleaning effect, and effectively protect the cutting parts, has a wide application prospect.
【技术实现步骤摘要】
一种环保耐腐蚀型切削液的制备方法
本专利技术涉及一种环保耐腐蚀型切削液的制备方法，属于切削液制备
技术介绍
金属切削过程是机械制造过程的一个重要组成部分。金属切削过程是指将工件上多余的金属层，通过切削加工被刀具切除而形成切屑并获得几何形状、尺寸精度和表面粗糙度都符合要求的零件的过程。合理使用切削液使切削温度和切削力得到最大限度的降低，提高刀具寿命和工件尺寸精度及表面质量，随着现代机械制造业的快速发展，切削技术和切削工艺的不断创新，对机械加工的配套材料金属切削液提出了更苛刻的要求。尤其是近年来环境保护和人类健康日益成为全社会关注的焦点，由于切削液会对环境和人体造成污染和损害，因此切削液的使用和废液的处理已受到环保法规日益严格的制约。为了适应社会发展的要求，现代切削液技术的发展出现了一些新的特点和趋势。大力开发对生态环境和人类健康负作用小、加工性能优越的切削液，朝着对人和环境完全无害的绿色切削液方向发展；同时，努力改进供液方法，优化供液参数和加强使用管理，以延长切削液的使用寿命，减少废液的排放量。众所周知，金属腐蚀的过程是金属与外围介质之间发生化学和电化学作...
【技术保护点】
一种环保耐腐蚀型切削液的制备方法，其特征在于具体制备步骤为：(1)选取新鲜豆渣，将其自然风干后研磨过40目筛，收集得豆渣颗粒，按质量比1:5，将豆渣颗粒与去离子水搅拌混合，随后在30～35℃下密封发酵处理5～7天，待其发酵完成后，过滤并收集滤液，将滤液加热煮沸处理10～15min后，再在75～80℃下旋转蒸发至原体积的1/5，制备得发酵豆渣浓缩液，备用；(2)收集新鲜菜籽饼，将其研磨并过40目筛，收集菜籽饼颗粒，按质量比1:10，将菜籽饼颗粒与石油醚搅拌混合，随后加热至回流处理6～8h后，过滤并收集滤饼，用无水乙醇冲洗3～5次后，自然晾干并研磨处理，随后过80目筛，收集得脱...
【技术特征摘要】
1.一种环保耐腐蚀型切削液的制备方法，其特征在于具体制备步骤为：(1)选取新鲜豆渣，将其自然风干后研磨过40目筛，收集得豆渣颗粒，按质量比1:5，将豆渣颗粒与去离子水搅拌混合，随后在30～35℃下密封发酵处理5～7天，待其发酵完成后，过滤并收集滤液，将滤液加热煮沸处理10～15min后，再在75～80℃下旋转蒸发至原体积的1/5，制备得发酵豆渣浓缩液，备用；(2)收集新鲜菜籽饼，将其研磨并过40目筛，收集菜籽饼颗粒，按质量比1:10，将菜籽饼颗粒与石油醚搅拌混合，随后加热至回流处理6～8h后，过滤并收集滤饼，用无水乙醇冲洗3～5次后，自然晾干并研磨处理，随后过80目筛，收集得脱脂菜籽饼颗粒；(3)按质量比...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。