一种耐热型高密度含能金属‑有机骨架材料及其制备方法技术

本发明专利技术公开了一种耐热型高密度含能金属‑有机骨架材料及其制备方法。该材料组成为[Pb(bta)(H2O)]n，其中bta为N,N′‑双四唑胺的负二价离子。制备方法是将配体加入去离子水中，用三乙胺调节体系pH值，随后加入Pb(NO3)2，充分搅拌后将混合物放入反应釜，程序升温至150°C并保持60h之后程序降至室温，得到无色立方晶体产物。本发明专利技术制得的材料具有高热稳定性（314˚C）、高密度（3.412 g·cm

A heat-resistant high density metal containing organic skeleton material and preparation method thereof

The invention discloses a heat resistant high density metal containing organic skeleton material and preparation method thereof. The material composition of [Pb (BTA) (H2O)]n, where BTA is the N, two negative valence ions N 'double four acetazolamide. The preparation method is the ligand of the deionized water, adjusting the pH value of the system with three ethylamine, then joined Pb (NO3) 2, stirring the mixture into a reaction kettle, heated to 150 DEG C and maintained after the 60H program to room temperature and get colorless cubic crystal products. The prepared material with high thermal stability (314 or C), high density (3.412 G - CM

【技术实现步骤摘要】
一种耐热型高密度含能金属-有机骨架材料及其制备方法
本专利技术涉及一种耐热型高密度含能金属-有机骨架材料，其可作为耐热的高能量密度材料用于火炸药或推进剂领域。
技术介绍
金属-有机骨架材料（简称MOFs），是由金属中心与桥连配体通过自组装相互连接，形成的一类具有周期性网络结构的晶态多孔材料。因其结构上的特点（高比表面积、结构性质可调、稳定性强等）已在气体存储与分离、发光、催化、药物传输等领域展现出良好的应用前景。近年来，金属-有机骨架材料在含能材料领域的应用逐步进入人们的视野。2012年，美国德州理工大学Hope-Weeks教授及其合作者报道了两个以肼及高氯酸根为配体的具有一维链状结构的材料[Ni(N2H4)5(ClO4)2)]n(NHP)和[Co(N2H4)5(ClO4)2)]n(CHP)，其爆热与著名的新型高能炸药CL-20（六硝基六氮杂异伍兹烷）相当（1.5kcal·g-1），由于链状结构的低刚度以及金属与肼的弱配位作用使其感度较高，难以应用。2013年，他们又以肼和肼的衍生物为配体得到了两个二维材料（[Co2(N2H4)4(N2H3CO2)2](ClO4)2·H2O(CHHP本文档来自技高网...

【技术保护点】
结构式为[Pb(bta)(H2O)]n的配合物，其中bta为N,N′‑双四唑胺的负二价离子，N,N′‑双四唑胺的负二价离子结构式为：

【技术特征摘要】
1.结构式为[Pb(bta)(H2O)]n的配合物，其中bta为N,N′-双四唑胺的负二价离子，N,N′-双四唑胺的负二价离子结构式为：该配合物属单斜晶系，P21/c空间群，晶胞参数为：a=10.607(16)(Å),b=6.572(10)(Å),c=11.396(17)(Å),α=90(deg),β=112.778(2)(deg),γ=90(deg)，摩尔质量为376.31g·mol-1。2.根据权利要求1所述的配合物，其特征在于：配合物热分解温度为314˚C，密度...

【专利技术属性】
技术研发人员：杨奇，宋霞霞，杨国利，谢钢，陈三平，高胜利，
申请(专利权)人：西北大学，
类型：发明
国别省市：陕西,61