The invention relates to a method for reducing the content of polycyclic aromatic hydrocarbons in a sludge based biological carbon. The preparation method is characterized in that: the elimination of the PAHs liquid and sludge based biochar in accordance with polycyclic aromatic hydrocarbons: eliminate liquid sludge based biochar = 1 ~ 3:1 volume ratio after mixing into the conical flask, the flask to avoid light environment within the concussion; remove the flask, remove the filter filtration liquid, solid left it will be shaped; solids with 1M hydrochloric acid solution 5min; the filter to the solids with hydrochloric acid, deionized water immersion 15min after filtration, deionized water soaking and filtering steps are repeated 3 times, and then put the filter into the oven to 105 DEG C dried to constant weight, to obtain carbon based biological sludge removal polycyclic aromatic hydrocarbons. The invention has the advantages that: by decreasing the content of PAHs in sludge based biochar, solve the effect of sludge biochar based on Soil and environment, reduce the safety risk of agricultural products, breaking the limit of sludge biochar based agriculture.
【技术实现步骤摘要】
一种降低污泥基生物炭中多环芳烃含量的方法
本专利技术涉及一种降低多环芳烃的技术方法,特别是涉及一种降低污泥基生物炭中多环芳烃含量的方法。
技术介绍
生物炭是指生物质在缺氧条件下经高温热解后剩下的物质。生物炭具有较大的比表面积和多孔结构,具有良好的吸附性能,可作为土壤改良剂,解决板结土壤透气性问题,提高土壤保肥保水的能力,促进作物生长。污泥中含有一定量的碳,可作为制备生物炭的原材料,将其制成污泥基生物炭,可用于污水处理、废气吸附、土壤改良等。目前公开的生物炭制备基材,多见于农林放弃物以及农林加工过程产生的放弃物。简要过程如下:(1)将废弃物进行处理,得到干燥的粉末状生物质原材料;(2)将生物质原材料置入绝氧并通保护气体且密封的处理器中,然后进行两阶段的升温处理,第一阶段的升温处理为从常温快速升温至220℃~260℃,第二阶段的升温处理为从第一阶段的终温慢速升至350℃~750℃,继续隔氧裂解1~3小时;(3)然后冷却至室温,将步骤(2)得到的物质依次经过研磨过筛、活化剂活化、蒸馏水洗涤和烘干后得到固体生物炭。生物炭的制备过程,固然原料易得,成本低廉,过程简单,当得到的生物炭中,残留有较多的多环芳烃,如苯并α芘,苯并α蒽等很多种多环芳烃具有致癌性,一旦多环芳烃进入土壤环境,对农作物和食品安全产生极大的威胁。尽管生物炭具有诸多优点,但因其通常是由不同类型的废弃物制备而得,制备的热解过程中常会导致多环芳烃的生成,尤其是市政污泥基生物炭,这就大大限制了污泥基生物炭应用范围与应用价值。本专利技术提供一种利用植物根系液去除污泥基生物炭中多环芳烃的技术方法,使其无害化,降 ...
【技术保护点】
一种降低污泥基生物炭中多环芳烃含量的方法,其特征在于:⑴将多环芳烃消除液与污泥基生物炭按照多环芳烃消除液:污泥基生物炭=1~3:1的体积比混合后移入锥形瓶,将锥形瓶避光环境内震荡;⑵取出锥形瓶,抽滤去除滤液,留下固形物;⑶将固形物用1M的盐酸浸洗5min;⑷滤去盐酸,将固形物用去离子水浸泡15min后过滤,去离子水浸泡与过滤步骤重复3遍,再把滤上物放入烘箱于105℃烘干至恒重,即获得除去多环芳烃的污泥基生物炭。
【技术特征摘要】
1.一种降低污泥基生物炭中多环芳烃含量的方法,其特征在于:⑴将多环芳烃消除液与污泥基生物炭按照多环芳烃消除液:污泥基生物炭=1~3:1的体积比混合后移入锥形瓶,将锥形瓶避光环境内震荡;⑵取出锥形瓶,抽滤去除滤液,留下固形物;⑶将固形物用1M的盐酸浸洗5min;⑷滤去盐酸,将固形物用去离子水浸泡15min后过滤,去离子水浸泡与过滤步骤重复3遍,再把滤上物放入烘箱于105℃烘干至恒重,即获得除去多环芳烃的污泥基生物炭。2.根据权利要求1所述的一种降低污泥基生物炭中多环芳烃的含量方法,其特征在于所述的无机盐培养液的配方为:3.根据权利要求1所述的一种降低污泥基生物炭中多环芳烃含量的方法,其特征在于所述的植物根系液制备过程如下:摘取草本植物的完整根系连同附着在根系上的土壤,放于研钵中湿磨得到该植物的根系残渣及残汁,即植物根系液。4.根据权利要求1所述的一种降低污泥基生...
【专利技术属性】
技术研发人员:郑育毅,陈琬,江娟,刘常青,刘文伟,吴春山,王菲凤,赵由才,李家兵,孙启元,谢蓉蓉,汪清环,
申请(专利权)人:福建师范大学,
类型:发明
国别省市:福建,35