一种铝合金基致密防腐MFI沸石膜的制备方法技术
Method for preparing aluminium alloy base dense corrosion resistant MFI zeolite membrane
The invention belongs to the field of metal surface corrosion protection coating, in particular to a preparation method of a dense corrosion resistant zeolite membrane, which comprises three steps of metal substrate pretreatment, sol preparation and hydrothermal synthesis. In situ synthesis of the invention adopts a anodic oxidation technology for pretreatment of Aluminum Alloy after zeolite membrane, the zeolite membrane than without zeolite membrane anodizing directly in situ growth is more compact, with excellent corrosion resistance. The preparation method has the advantages of convenient operation and no metal substrate shape, is the development of new technology of dense zeolite coating for anticorrosion, high mechanical strength of the prepared zeolite coating, coating with good adhesion and environmentally friendly, so the popularization of the invention has good social, environmental and economic benefits.
【技术实现步骤摘要】
一种铝合金基致密防腐MFI沸石膜的制备方法
本专利技术属于金属表面防腐、耐磨功能涂层制备
，具体涉及一种在阳极氧化后的铝合金表面原位生长致密沸石涂层的方法，使得铝合金表面耐腐蚀性大大提高，实现沸石膜在金属防腐方面的应用。
技术介绍
铝合金是工业界广泛应用的一类金属，金属铝比强度与比刚度高、可加工性强且资源丰富，可以预见铝合金在未来仍是最重要的金属材料之一。然而铝合金应用过程中的腐蚀不容忽视，铝合金的腐蚀一方面造成浪费，另一方面使得铝合金制件存在极大的安全隐患。以金属防腐涂层为着眼点，目前世界各国开发了多种铝合金防腐技术，主要有阳极氧化、化学转化膜、电镀以及化学镀等。其中高效而得到广泛使用的是含铬化学转化膜，比较典型的是达克罗(DCROMET)涂层(锌铬涂层)，然而此类涂层在生产和使用过程中会释放致癌性的六价铬，对生物体毒害较大。因此，新型高效而环境友好型无铬转化防腐涂层的开发是工业界与学术界关注的焦点。沸石是一类微孔硅铝酸盐的晶体(孔径小于0.2nm)，人们常利用它的多孔结构来分离分子尺度的物质，因此又叫分子筛。沸石膜早期的应用主要集中在物质的分离和催化过程...
【技术保护点】
一种铝合金基致密防腐沸石膜的制备方法，其特征在于，所述的方法包括如下步骤：(1)基底前处理：将铝合金基片进行丙酮超声清洗，清洗后接入装有电解质溶液的电解槽正极进行阳极氧化处理，设定电流密度为10～15mA/cm
【技术特征摘要】
1.一种铝合金基致密防腐沸石膜的制备方法，其特征在于，所述的方法包括如下步骤：(1)基底前处理：将铝合金基片进行丙酮超声清洗，清洗后接入装有电解质溶液的电解槽正极进行阳极氧化处理，设定电流密度为10～15mA/cm2，时间为30～60分钟，电解过程中电解液温度不超过26℃；(2)合成溶胶配制：将分析纯正硅酸乙酯、质量分数为25％的四丙基氢氧化铵、高纯铝箔、分析纯氢氧化钠与去离子水按照1∶0.12～0.2∶0～0.1∶0.50～0.7∶30～100的摩尔配比进...
【专利技术属性】
技术研发人员：仝晓强，张娜，安冬敏，成业，周青军，
申请(专利权)人：中国民航大学，